FRIANYL® A3 RV0 is an unfilled Polyamide 66 (Nylon 66) compound,heat stabilized, flame retardant, halogen and red phosphorous free,UL listed V0.
It is VDE certified. It is also certified according to railwaysrequirements EN45545-2 and NFF 16-101.
This compound is intended for injection molding.
FRIANYL® A3 RV0 is primarily designed for the Electrical andElectronic industry. It is also suitable for Automotive orIndustrial & Consumer applications.
| |
| 特性 |
|
| 用途 |
|
| 加工方法 |
|
| 密度 (23°C) | 1.15 | g/cm³ | ISO 1183 |
| 收缩率 | ISO 294-4 | ||
| 垂直流动方向 :23°C | 1.6 | % | ISO 294-4 |
| 流动方向 :23°C | 1.5 | % | ISO 294-4 |
| 吸水率 | ISO 62 | ||
| 23°C, 24hr | 1.4 | % | ISO 62 |
| 饱和, 23°C | 6.0 | % | ISO 62 |
| 拉伸模量 (23°C) | 3400 | MPa | ISO 527-2 |
| 拉伸应力 (屈服, 23°C) | 85.0 | MPa | ISO 527-2 |
| 拉伸应变 (断裂, 23°C) | 12 | % | ISO 527-2 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | ISO 179/1eA |
| 23°C | 3.5 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 | ISO 179/1eU | ||
| 23°C | 无断裂 | ISO 179/1eU | |
| 30°C | 无断裂 | ISO 179/1eU |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度 | |||
| 0.45 MPa,未退火 | 185 | °C | ISO 75-2/B |
| 1.8 MPa,未退火 | 85.0 | °C | ISO 75-2/A |
| 连续使用温度 1 | 130 | °C | IEC 60216 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | IEC 60695-10-2 | |
| 165°C | Pass | IEC 60695-10-2 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 表面电阻率 2 | 1.0E+13 | ohms | IEC 60093 |
| 体积电阻率 (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
| 介电强度 (2.00 mm) | 25 | kV/mm | IEC 60243-1 |
| 漏电起痕指数 (3.20 mm, 解决方案 A) | 600 | V | IEC 60112 |
| 针焰试验 | IEC 60695-11-5 | ||
| 1.00 mm | 通过 | IEC 60695-11-5 | |
| 2.00 mm | 通过 | IEC 60695-11-5 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL 阻燃等级 | UL 94 | ||
| 0.400 mm | V-0 | UL 94 | |
| 0.800 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| 灼热丝易燃指数 | IEC 60695-2-12 | ||
| 0.800 mm | 960 | °C | IEC 60695-2-12 |
| 3.20 mm | 960 | °C | IEC 60695-2-12 |
| 热灯丝点火温度 | IEC 60695-2-13 | ||
| 0.800 mm | 775 | °C | IEC 60695-2-13 |
| 3.20 mm | 775 | °C | IEC 60695-2-13 |
| 极限氧指数 | 33 | % | ISO 4589-2 |
| 可燃性 3 | SE | FMVSS 302 |