Celstran® PA66-GF40-02P11
Polyamide 66
Celanese Corporation
40% 长玻璃纤维
产品说明：
Material code according to ISO 1043-1: PA66
Nylon 66 reinforced by 40 weight percent long glass
fibers. The pellets are cylindrical and normally as well as the
embedded fibers 10 mm long.
Parts molded of CELSTRAN have outstanding mechanical propertiessuch
as high strength and stiffness combined with high heatdeflection.
The notched impact strength is increased at elevated and low
temperatures due to the fiber skeleton built in the parts. Thelong
fiber reinforcement reduces creep significantly.
The very isotropic shrinkage in the molded parts minimizes the
warpage.
Complex parts can be manufactured with high reproducibility by
injection molding.
Can be used for substituting die cast metal with the advantageof
Weight reduction, no corrosion problems, no posttreatment.
| 填料/增强材料 |
|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 加工方法 |
|
| 树脂ID (ISO 1043) |
|
| 拉伸模量 | 13000 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (断裂) | 215 | MPa | ISO 527-2/1A/5 |
| 拉伸应变 (断裂) | 2.0 | % | ISO 527-2/1A/5 |
| 弯曲模量 (23°C) | 8100 | MPa | ISO 178 |
| 弯曲应力 (23°C) | 200 | MPa | ISO 178 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 70.0 到 80.0 | °C | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的*大水分含量 | 0.15 | % | |
| 料斗温度 | 70.0 到 80.0 | °C | |
| 料筒后部温度 | 280 到 285 | °C | |
| 料筒中部温度 | 280 到 290 | °C | |
| 料筒前部温度 | 290 到 300 | °C | |
| 射嘴温度 | 310 到 320 | °C | |
| 加工（熔体）温度 | 310 到 320 | °C | |
| 模具温度 | 90.0 到 120 | °C | |
| 注塑压力 | 120 到 150 | MPa | |
| 注射速度 | 中等 | ||
| 保压 | 50.0 到 80.0 | MPa | |
| 背压 | 0.00 到 3.00 | MPa |