Celstran®PA66-GF60-02 P11/14
Polyamide 66
Celanese Corporation
60% 长玻璃纤维
产品说明：
Material code according to ISO 1043-1: PA66
Heat stabilized Nylon 66 reinforced by 60 weight percent longglass
fibers. The pellets are cylindrical and normally as well as the
embedded fibers 11 mm long.
Parts molded of CELSTRAN have outstanding mechanical propertiessuch
as high strength and stiffness combined with high heatdeflection.
The notched impact strength is increased at elevated and low
temperatures due to the fiber skeleton built in the parts. Thelong
fiber reinforcement reduces creep significantly.
The very isotropic shrinkage in the molded parts minimizes the
warpage.
Complex parts can be manufactured with high reproducibility by
injection molding.
Can be used for substituting die cast metal with the advantageof
Weight reduction, no corrosion problems, no post treatment.
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 加工方法 |
|
| 树脂ID (ISO 1043) |
|
| 干燥温度 | 70.0 到 80.0 | °C | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的*大水分含量 | 0.15 | % | |
| 料斗温度 | 70.0 到 80.0 | °C | |
| 料筒后部温度 | 280 到 285 | °C | |
| 料筒中部温度 | 280 到 290 | °C | |
| 料筒前部温度 | 290 到 300 | °C | |
| 射嘴温度 | 310 到 320 | °C | |
| 加工（熔体）温度 | 310 到 320 | °C | |
| 模具温度 | 90.0 到 120 | °C | |
| 注塑压力 | 120 到 150 | MPa | |
| 注射速度 | 中等 | ||
| 保压 | 50.0 到 80.0 | MPa | |
| 背压 | 0.00 到 3.00 | MPa |
产品说明：
60% 长玻璃纤维,低翘曲性,刚性高,高强度,抗撞击性良好,良好的抗蠕变性,耐低温冲击,热稳定性