美国杜邦PA6 73G15L NC010加纤尼龙15%
杜邦® 73G15L NC010尼龙树脂15% 玻璃纤维增强材料杜邦高性能聚合物产品说明：15%玻璃纤维增强聚酰胺6
Zytel® 73G15L NC010 物性表
| 基本信息 | |
|---|---|
| 黄卡编号 |
|
| 填料/增强材料 |
|
| 添加剂 |
|
| 特性 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 多点数据 |
|
| 部件标识代码 (ISO 11469) |
|
| 树脂ID (ISO 1043) |
|
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 密度 | 1.23 | -- | g/cm³ | ISO 1183 |
| 收缩率 | ISO 294-4 | |||
| 垂直流动方向 | 0.80 | -- | % | ISO 294-4 |
| 流动方向 | 0.30 | -- | % | ISO 294-4 |
| 吸水率 | ISO 62 | |||
| 23°C, 24 hr,2.00 mm | 7.6 | -- | % | ISO 62 |
| 平衡, 23°C, 2.00mm, 50% RH | 2.5 | -- | % | ISO 62 |
| 粘数 | 150 | -- | cm³/g | ISO 307 |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 拉伸模量 | 6000 | 3500 | MPa | ISO 527-2 |
| 拉伸应力 (断裂) | 135 | 72.0 | MPa | ISO 527-2 |
| 拉伸应变 (断裂) | 4.0 | 10 | % | ISO 527-2 |
| 弯曲模量 | 5000 | -- | MPa | ISO 178 |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA | |||
| -40°C | 6.0 | -- | kJ/m² | ISO 179/1eA |
| -30°C | 6.0 | 14 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | 15 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 | ISO 179/1eU | |||
| -30°C | 45 | 54 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | 95 | kJ/m² | ISO 179/1eU |
| 悬壁梁缺口冲击强度 | ISO 180/1A | |||
| -40°C | 5.0 | -- | kJ/m² | ISO 180/1A |
| -30°C | 5.0 | -- | kJ/m² | ISO 180/1A |
| 23°C | 6.0 | 12 | kJ/m² | ISO 180/1A |
| 无缺口伊佐德冲击强度 | ISO 180/1U | |||
| -40°C | 40 | -- | kJ/m² | ISO 180/1U |
| 23°C | 45 | -- | kJ/m² | ISO 180/1U |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 热变形温度 | ||||
| 0.45 MPa,未退火 | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa,未退火 | 200 | -- | °C | ISO 75-2/A |
| 维卡软化温度 | 215 | -- | °C | ISO 306/B50 |
| 熔融温度 1 | 221 | -- | °C | ISO 11357-3 |
| 线形热膨胀系数 | ISO 11359-2 | |||
| 流动 | 3.7E-5 | -- | cm/cm/°C | ISO 11359-2 |
| 横向 | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| 可燃性 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 燃烧速率 2(1.00 mm) | 25 | -- | mm/min | ISO 3795 |
| 可燃性等级 (1.50 mm) | HB HB | -- | IEC 60695-11-10, -20 | |
| 极限氧指数 | 21 | -- | % | ISO 4589-2 |
| 充模分析 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 熔体密度 | 1.07 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2470 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.19 | -- | W/m/K |
| 补充信息 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| Emission of Organic Compounds | 8.50 | -- | µgC/g | VDA 277 |
| Odor | 4 | -- | VDA 270 |
美国杜邦PA6 73G15L NC010加纤尼龙15%
LUBRICOMPCompound RFL36XXY LUBRICOMPRFL36XXY is a compound based on Nylon 66 containing 30% GlassFiber, 15% PTFE. Added feature of this grade is: WearResistant.
LUBRICOMPCompound RCL26 LUBRICOMPRCL26 is a compound based on Nylon 66 containing 30% Carbon Fiber,10% PTFE. Added features of this grade include: Wear Resistant,Electrically Conductive.
LUBRICOMPCompound RBL36XXJ LUBRICOMPRBL36XXJ is a compound based on Nylon 66 containing 30% Glass Bead,15% PTFE. Added features of this grade include: Low Extractable,Healthcare, Wear Resistant.
LUBRICOMPCompound RAL23S LUBRICOMP RAL23Sis a compound based on Nylon 66 resin containing 10% PTFE, 15%Aramid. Added features of this material include: Heat Stabilized,Wear Resistant.
LUBRICOMPCompound RAL22S LUBRICOMPRAL22S is a compound based on Nylon 66 resin containing 10% PTFE,10% Aramid. Added features of this material include: WearResistant.
LUBRICOMPCompound RAP22 LUBRICOMPRAP22 is a compound based on Nylon 66 resin containing 10% Aramid,10% PTFE/Silicone. Added feature of this grade includes: WearResistant.
LUBRICOMPCompound RBG16I LUBRICOMPRBG16I is a compound based on Nylon 66 resin containing Glass Bead,Graphite. Added features of this material include: HighImpact.
LUBRICOMPCompound RFN16S LUBRICOMP RFN16Sis a compound based on Nylon 66 resin containing 30% Glass Fiber,5% MOS2. Added features of this material include: Heat Stabilized,Wear Resistant.
LUBRICOMPCompound RFN16SXZ LUBRICOMP RFN16SXZis a compound based on Nylon 66 resin containing 30% Glass Fiber,5% MOS2. Added features of this material include: Heat Stabilized,Wear Resistant.
LUBRICOMPCompound RFN17SXS LUBRICOMPRFN17SXS is a compound based on Nylon 66 resin containing GlassFiber, MOS2. Added features of this material include: HeatStabilized
LUBRICOMPCompound RL002 LUBRICOMP RL002 is a compound based on Nylon66 resin
美国杜邦PA6 73G15LNC010加纤尼龙15%
Polymaker宣布推出两款新型3D打印材料：碳纤维增强PA6和玻璃纤维填充PA6。
这两种材料均由该公司的纤维粘合技术开发而成，该技术增强了印刷部件在X，Y和Z轴上的层间粘合性。由于是增强纤维，PolyMidePA6-CF和PolyMide PA6-GF还具有高强度和高热变形温度，使其能够在苛刻的环境中被使用。
PolyMidePA6-CF是碳纤维增强等级，具有Polymaker全部材料组合的高强度，抗冲击性和热变形(215℃)。它也是一种ESD安全材料，适用于电子夹具和固定装置以及汽车应用的生产。
同时，PolyMidePA6-GF是一种玻璃纤维填充材料，具有良好的强度和刚度。其热性能和机械性能意味着它可用于在广泛的温度范围内打印零件。该材料已用于生产工作温度低至-190℃的定制实验室设备。
美国杜邦PA6 73G15L NC010加纤尼龙15%
通过Polymaker的纤维粘合技术，它们还能改善层间粘合性。该技术可优化纤维的表面化学性质，从而增强分散性并与聚酰胺基质结合。与使用纯PA6材料印刷的部件相比，这相应增加了Z轴上的强度，降低的各向异性。纤维粘合技术旨在解决纤维与材料结合时的层间粘附问题，并使Polymaker能够将PolyMidePA6-CF和PolyMide PA6-GF推向市场。
Polymaker的新产品已经被应用于一家位于上海的研究实验室。该实验室专注于研究模拟主要由氢和氦组成的行星核心条件的环境，如土星和木星。HPStar已经实施了3D打印，以创建包含钢制单元的电池座，以夹持两颗钻石之间的氢气。然后红外激光通过钻石射入高压室。当钢制电池收紧时产生，并将金刚石夹在一起，这样就能重现行星核心的极端温度和压力。