美国杜邦PA6 7300T NC010
杜邦® BM7300THS BK317型尼龙树脂杜邦高性能聚合物产品说明：增韧，热稳定，聚酰胺6吹塑成型开发
Zytel® BM7300THS BK317 物性表
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 加工方法 |
|
| 多点数据 |
|
| 部件标识代码 (ISO 11469) |
|
| 树脂ID (ISO 1043) |
|
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 密度 | 1.09 | -- | g/cm³ | ISO 1183 |
| 收缩率 | ISO 294-4 | |||
| 横向流量 | 1.1 | -- | % | ISO 294-4 |
| 流量 | 1.1 | -- | % | ISO 294-4 |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 拉伸模量 | 2200 | 600 | MPa | ISO 527-2 |
| 拉伸应力 (屈服) | 60.0 | -- | MPa | ISO 527-2 |
| 拉伸应变 (屈服) | 4.2 | -- | % | ISO 527-2 |
| 标称拉伸断裂应变 | > 50 | -- | % | ISO 527-2 |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA | |||
| -30°C | 21 | 22 | kJ/m² | ISO 179/1eA |
| 23°C | 45 | 150 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 | ISO 179/1eU | |||
| -30°C1 | 无断裂 | 无断裂 | ISO 179/1eU | |
| 23°C | 无断裂 | 无断裂 | ISO 179/1eU | |
| 悬壁梁缺口冲击强度 | ISO 180/1A | |||
| -30°C | 18 | 20 | kJ/m² | ISO 180/1A |
| 23°C | 38 | 120 | kJ/m² | ISO 180/1A |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 热变形温度 | ||||
| 0.45 MPa,未退火 | 100 | -- | °C | ISO 75-2/B |
| 1.8 MPa,未退火 | 52.0 | -- | °C | ISO 75-2/A |
| 熔融温度 2 | 220 | -- | °C | ISO 11357-3 |
| 可燃性 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 燃烧速率 3(1.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| FMVSS 可燃性 | B | -- | FMVSS 302 |
| 注射 | 干燥 | 单位制 | |
|---|---|---|---|
| Melt Temperature, Optimum | 270 | °C | |
| Mold Temperature, Optimum | 70 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm | |
| Maximum Screw Tangential Speed | 200 | mm/sec |
| 充模分析 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 熔体粘度 (280°C, 1000 sec^-1) | 440000 | -- | mPa·s | ISO 11443 |
| 注射 | 干燥 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 80 | °C | |
| 干燥时间 - 热风干燥机 | 2.0 到 4.0 | hr | |
| 建议的大水分含量 | 0.20 | % | |
| 加工（熔体）温度 | 260 到 280 | °C | |
| 模具温度 | 50 到 100 | °C | |
| 保压 | 50.0 到 100 | MPa |
美国杜邦PA6 7300T NC010
LUBRICOMPCompound IFL36L LUBRICOMPIFL36L is a compound based on Nylon 6/12 containing 30% GlassFiber, 15% PTFE. Added features of this grade include: LowExtractable, Wear Resistant.
LUBRICOMPCompound IL004 LUBRICOMPIL004 is a compound based on Nylon 6/12 resin containing 20% PTFE.Added features of this material include: WearResistant.
LUBRICOMPCompound IFL36RInternallylubricated PA6.12, containing Glass Fiber andPTFE
LUBRICOMPCompound RCL36S LUBRICOMP RCL36Sis a compound based on Nylon 66 resin containing 30% Carbon Fiber,15% PTFE. Added features of this material include: ElectricallyConductive, Wear Resistant...
LUBRICOMPCompound SCL36 LUBRICOMPSCL36 is a compound based on Nylon 12 resin containing 15% PTFE,30% Carbon Fiber. Added features of this material include: WearResistant, Electrically Conductive.
LUBRICOMPCompound RCL26 LUBRICOMPRCL26 is a compound based on Nylon 66 containing 30% Carbon Fiber,10% PTFE. Added features of this grade include: Wear Resistant,Electrically Conductive.
LUBRICOMPCompound RBL36XXJ LUBRICOMPRBL36XXJ is a compound based on Nylon 66 containing 30% Glass Bead,15% PTFE. Added features of this grade include: Low Extractable,Healthcare, Wear Resistant.
LUBRICOMPCompound RAL23S LUBRICOMP RAL23Sis a compound based on Nylon 66 resin containing 10% PTFE, 15%Aramid. Added features of this material include: Heat Stabilized,Wear Resistant.
LUBRICOMPCompound RAL22S LUBRICOMPRAL22S is a compound based on Nylon 66 resin containing 10% PTFE,10% Aramid. Added features of this material include: WearResistant.
LUBRICOMPCompound RAP22 LUBRICOMPRAP22 is a compound based on Nylon 66 resin containing 10% Aramid,10% PTFE/Silicone. Added feature of this grade includes: WearResistant.
LUBRICOMPCompound RBG16I LUBRICOMPRBG16I is a compound based on Nylon 66 resin containing Glass Bead,Graphite. Added features of this material include: HighImpact.
LUBRICOMPCompound RFN16S LUBRICOMP RFN16Sis a compound based on Nylon 66 resin containing 30% Glass Fiber,5% MOS2. Added features of this material include: Heat Stabilized,Wear Resistant.
美国杜邦PA6 7300T NC010
巴斯夫完成了对索尔维聚酰胺(PA6.6)业务的收购。巴斯夫就此项交易在无现金和无债务基础上支付的购买价格达13亿欧元;被巴斯夫收购的索尔维相关业务2018年的销售额约为10亿欧元。该业务将整合入巴斯夫特性材料业务部和单体业务部。
巴斯夫欧洲公司执行董事会成员 Wayne T. Smith表示：“我们的客户将极大受益于巴斯夫更加广泛的产品组合、更强的区域影响力以及更可靠的供应。此次收购代表了我们对全球聚酰胺业务的坚定投入。”
索尔维与巴斯夫之间的交易包括索尔维在德国、法国、中国、印度、韩国、巴西和墨西哥的共计八个生产基地，以及在亚洲、北美和南美的研发中心和技术咨询中心。此外，交易还包括法国两家合资企业的股份，即：索尔维在其与英威达成立的合资工厂Butachimie里50%的股份，该工厂主要生产己二腈(ADN)和六亚甲基二胺(HMD);以及巴斯夫和道默化学新成立的合资企业Alsachimie 51%的股份，该工厂主要产生己二酸。
美国杜邦PA6 7300T NC010
交易完成后， 将有约700名索尔维员工加入巴斯夫。巴斯夫与道默化学在法国成立的合资企业Alsachimie拥有约650名员工，巴斯夫与英威达建立的合资企业Butachimie拥有约400名员工。
2017年9月，巴斯夫与索尔维签署了一项关于收购索尔维整体聚酰胺业务的协议，并交由相关监管机构的批准。2019年1月18日，欧盟委员会批准了巴斯夫在符合相关条件的前提下收购聚酰胺业务，要求将原始交易范围的一部分，即索尔维聚酰胺业务在欧洲的生产装置及创新能力，剥离转让给第三方买家。总部位于德国洛伊纳(Leuna)的道默化学获得欧盟委员会批准成为买家。索尔维与道默化学亦于2020年1月31日完成相关交易。
通过这项交易，巴斯夫将的创新产品如Technyl®品牌纳入麾下，拓展了聚酰胺业务的实力。巴斯夫得以为客户提供更出色的工程塑料解决方案，比如在自动驾驶和电动出行领域。该项交易的达成还有助于巴斯夫更好地进入亚洲、北美和南美等主要增长市场。通过整合上游关键原料己二腈(ADN)，巴斯夫将整体强化聚酰胺6.6价值链，提高供应可靠性。
美国杜邦PA6 7300T NC010