经销沙伯基础汽车空调外壳PPE/PS NORYL EM6100
Density / Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | cm³/10min | ISO 1133 | |
Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
Water Absorption (24 hr) | 0.20 | ASTM D570 |
Tensile Modulus | |||
-- 2 | 1900 | MPa | ASTM D638 |
-- | 2050 | ISO 527-2/1 | |
Tensile Strength | |||
Yield 3 | 43.0 | ASTM D638 | |
Yield | 42.0 | ISO 527-2 | |
Break | 40.0 | ASTM D638, ISO 527-2 | |
Tensile Elongation | |||
Yield | 3.0 | 2.8 | ISO 527-2 |
Break 3 | 65 | ASTM D638 | |
Break | 60 | ISO 527-2 | |
Flexural Modulus | |||
50.0 mm Span 4 | 2100 | ASTM D790 | |
100 mm Span 5 | 2000 | ASTM D790 | |
-- | ISO 178 | ||
Flexural Stress | |||
-- | 65.0 | ISO 178 | |
Yield, 50.0 mm Span 4 | 67.0 | ASTM D790 | |
Yield, 100 mm Span 5 | 66.0 | ASTM D790 | |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/2C | ||
-30°C | 19 | kJ/m² | |
23°C | 33 | ||
Notched Izod Impact | |||
-30°C | 250 | J/m | ASTM D256 |
23°C | 450 | ASTM D256 | |
-30°C 6 | ISO 180/1A | ||
23°C 6 | ISO 180/1A | ||
Instrumented Dart Impact | ASTM D3763 | ||
-30°C, Energy at Peak | 24.0 | J | |
23°C, Energy at Peak | 36.0 | ||
23°C, Total Energy | 42.0 | J |