美国沙比克高抗疲劳PPO NORYL HNA055
>PPE+PS-HI
Density / Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 6.2 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 5.00 | cm³/10min | ISO 1133 |
Molding Shrinkage - Flow (3.20 mm) | 0.60 to 0.80 | % | Internal Method |
Water Absorption | ISO 62 | ||
Saturation, 23°C | 0.23 | ||
E, 23°C, 50% RH | 0.060 |
Charpy Notched Impact Strength 6 (23°C) | 27 | kJ/m² | ISO 179/1eA |
Notched Izod Impact | |||
-30°C | 140 | J/m | ASTM D256 |
23°C | 290 | ASTM D256 | |
-30°C 7 | 14 | ISO 180/1A | |
23°C 7 | 24 | ISO 180/1A | |
Instrumented Dart Impact (23°C, Total Energy) | 54.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
1.8 MPa, Unannealed, 3.20 mm | 147 | °C | ASTM D648 |
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 7 | ISO 75-2/Af |