原包沙伯基础PPE/PS NORYL N750无卤阻燃高流动
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 28 g/10 min @Load 3.80 kg, Temperature 260 °C | 28 g/10 min @Load 8.38 lb, Temperature 500 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 25 % | 25 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.34 GPa | 339 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 75.0 MPa | 10900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 31.0 J @Temperature 23.0 °C | 22.9 ft-lb @Temperature 73.4 °F | ASTM D3763 |