现货出售PA66日本东丽CM3001G-30 注塑级尼龙，30%玻纤增强 汽车配件原料
日本东丽PA66 CM3001G-30物性表
| PA66 CM3001G-30 日本东丽工业株式会社物性数据 |
①原料描述部分| 规格级别： | 注塑级 | 外观颜色： | --- |
| 用途概述： | 一般用途 |
| 备注说明： | 特性：玻纤增强30% |
②原料技术数据| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据无水1.5%水 | 数据单位 |
| 基本性能 | 吸水率 | 23℃ | ASTM D-570 | 0.6- | % |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.37- | --- |
| 泰伯磨耗量 | (1000g,CS-17)23℃ | ASTM D-1044 | 24- | mg/1000次 |
| 机械性能 | 洛氏硬度 | 23℃ | ASTM D-785 | 97- | M-标度 |
| 压缩强度 | 80℃ | ASTM D-695 | 1100- | Kg/cm2 |
| 抗剪强度 | 23℃ | ASTM D-732 | 970830 | Kg/cm2 |
| 抗剪强度 | 80℃ | ASTM D-732 | 760- | Kg/cm2 |
| IZOD冲击强度 | -40℃，V缺口1/2 | ASTM D-256 | 810 | kg・cm/cm |
| IZOD冲击强度 | 23℃，V-缺口1/2 | ASTM D-256 | 914 | kg・cm/cm |
| IZOD冲击强度 | -40℃ | --- | 6070 | kg・cm/cm2 |
| IZOD冲击强度 | 23℃，无缺口1/8 | --- | 6578 | kg・cm/cm2 |
| 洛氏硬度 | 23℃ | ASTM D-785 | 121- | R-标度 |
| 抗拉屈服强度 | -40℃ | ASTM D-638 | 23502100 | Kg/cm2 |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 18001350 | Kg/cm2 |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 1100900 | Kg/cm2 |
| 断裂伸长率 | -40℃ | ASTM D-638 | 3.5- | % |
| 断裂伸长率 | 23℃ | ASTM D-638 | 55 | % |
| 断裂伸长率 | 80℃ | ASTM D-638 | 8.5- | % |
| 挠曲强度 | -40℃ | ASTM D-790 | 3000- | Kg/cm2 |
| 挠曲强度 | 23℃ | ASTM D-790 | 26001900 | Kg/cm2 |
| 挠曲强度 | 80℃ | ASTM D-790 | 17501250 | Kg/cm2 |
| 挠曲模量 | -40℃ | ASTM D-790 | 8500060000 | Kg/cm2 |
| 挠曲模量 | 80℃ | ASTM D-790 | 5000040000 | Kg/cm2 |
| 压缩强度 | -40℃ | ASTM D-695 | 2600- | Kg/cm2 |
| 压缩强度 | 23℃ | ASTM D-695 | 1850- | Kg/cm2 |
| 电气性能 | 体积电阻率 | --- | ASTM D-257 | 10151012-1013 | Ω.cm |
| 介电强度 | 1/8" | ASTM D-149 | 2017 | KV/mm |
| 介电常数 | 50Hz | ASTM D-150 | 4.66.3 | --- |
| 介电常数 | 103Hz | ASTM D-150 | 4.45.5 | --- |
| 介电常数 | 106Hz | ASTM D-150 | 3.94.0 | --- |
| 损耗因数 | 50Hz | ASTM D-150 | 0.020.08 | --- |
| 损耗因数 | 103Hz | ASTM D-150 | 0.020.08 | --- |
| 损耗因数 | --- | ASTM D-150 | 0.02- | --- |
| 抗电弧性 | 1/8" | ASTM D-495 | 114120 | s |
| 热 性 能 | UL-94抗燃级 | 1/16" | UL 94 | HB- | --- |
| 熔点 | --- | 差示扫描测热计DSC | 265- | ℃ |
| 比热 | --- | --- | 0.38- | Cal/g・℃ |
| 导热系数 | --- | --- | 0.02- | Kcal/m・hr・℃ |
| 线性热膨胀系数 | --- | ASTM D-696 | 2-3- | ×10-5cm/cm/℃ |
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 262- | ℃ |
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 255- | ℃ |
| 其它性能 | 强化含量 | --- | --- | 30- | WT% |