POM C13031泰科纳POM copolymer
Easy flowing Injection molding type like C 13021, but withhigher
strength, rigidity and hardness over the entire permissible
temperature range for HOSTAFORM; good chemical resistance to
solvents, fuel and strong alkalis as well as good hydrolysis
resistance; high resistance to thermal and oxidativedegradation.
Monomers and additives are listed in EU-Regulation (EU) 10/2011
FDA compliant according to 21 CFR 177.2470
UL-registration for all colours and a thickness more than 1.5 mmas
UL 94 HB; burning rate ISO 3795 and FMVSS 302 < 75 mm/min fora
thickness more than 1 mm.
Ranges of applications: For molded parts with higher requirementsto
strength, rigidity und hardness, ranges of applications withfuel
POM C13031泰科纳相关型号：
POM(聚甲醛#赛钢)/C13031XF/泰科纳 用途： 其它 重要参数： 熔体流动速率:12 g/10min 密度:1.42g/cm3 吸水率:0.3 % 成型收缩率:1.9 % 弯曲模量:2900 MPa 热变形温度:159 ℃生产厂商：美国泰科纳公司
POM(聚甲醛#赛钢)/C13031K/泰科纳 用途： 其它 特性备注：耐化学性，水解性，和氧化性 重要参数：熔体流动速率:11 g/10min 密度:1.44 g/cm3 吸水率:0.65 % 成型收缩率:2 % 维卡软化点:156 ℃热变形温度:105 ℃ 生产厂商：美国泰科纳公司
POM(聚甲醛#赛钢)/C13031/美国塞拉尼斯 用途： 家用电器,汽车部件,运动器材 重要参数： 熔体流动速率:16.92g/10min 密度:1.41 g/cm3 缺口冲击强度:0.6 断裂伸长率:20 % 弯曲模量:3000 MPa 维卡软化点:158℃ 热变形温度:112 ℃ 生产厂商：美国塞拉尼斯公司
POM C13031泰科纳注射：
干燥温度 120 到 140 °C 干燥时间 3.0 到 4.0 hr 建议的Zui大水分含量 0.15 % 料斗温度 20.0 到30.0 °C 料筒后部温度 170 到 180 °C 料筒中部温度 180 到 190 °C 料筒前部温度 190 到 200 °C射嘴温度 190 到 210 °C 加工（熔体）温度 190 到 210 °C 模具温度 80.0 到 120 °C 注塑压力60.0 到 120 MPa 注射速度 慢到中等 保压 60.0 到 120 MPa 背压 0.00 到 4.00 MPa