Orevac® T9307 Y
Ethylene Vinyl Acetate Copolymer
Arkema
产品说明：
OREVAC® T 9307 Y is a random terpolymer of ethylene, vinylacetate and maleic anhydride made by high-pressure radicalarpolymerization process. As an ethylene copolymer, OREVAC® T 9307 Yis compatible with PE in all proportions, and with most otherethylene copolymers. Vinyl acetate brings softness, flexibility andpolarity, maleic anhydride gives reactivity, leading to versatileadhesive properties to polar and non polar substrates. As a resultof high-pressure polymerisation in tubular reactor, OREVAC® T 9307Y exhibits high transparency (low haze).
Applications
OREVAC® T 9307 Y is suitable to produce thermo-adhesive films forsolid substrates like PA, PET & PU films, aluminium foils, fibermats, foams... OREVAC® T 9307 Y can also be used as a skinpackaging adhesive on all type of cardboard.
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.939 | g/cm³ | ISO 1183, ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 9.5 到 12 | g/10 min | ASTM D1238, ISO 1133 |
| 醋酸乙烯含量 | 13.0 到 15.0 | wt% | |
| Maleic Anhydride Content | 1600 | ppm |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Ring and Ball Softening Point | 145 | °C | ASTM E28 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 A, 15 秒, 2.80 mm,模压成型) | 91 | ASTM D2240, ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | |||
| 断裂, 2.80 mm,模压成型 1 | 19.0 | MPa | ASTM D638 |
| 断裂, 2.80 mm,模压成型 | 19.0 | MPa | ISO 527-2/5A/50 |
| 伸长率 | |||
| 断裂, 2.80 mm,模压成型 2 | 700 到 900 | % | ASTM D638 |
| 断裂, 2.80 mm,模压成型 | 700 到 900 | % | ISO 527-2/5A/50 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 66.0 | °C | ISO 306/A, ASTM D1525 3 |
| 熔融温度 | 93.0 | °C | ISO 11357-3 |
| 备注 | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 压 力1 (10N) |