原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔融指数 | 220℃/10kg | ASTM D-1238 | 35 | g/10min |
| 物理性能 | 比重 | ASTM D-792 | 1.20 | ||
| 模具收缩率 | ASTM D-955 | 0.4-0.8 | % | ||
| 机械性能 | 拉伸强度 | 50mm/min | ASTM D-638 | 410 | kg/cm2 |
| 440伸长率 | 50mm/min | ASTM D-638 | 15 | % | |
| 抗弯强度 | 15mm/min | ASTM D-790 | 710 | kg/cm2 | |
| 抗弯模数 | 15mm/min | ASTM D-790 | 24000 | kg/cm2 | |
| IZOD缺口冲击强度 | Notched 1/4" | ASTM D-256 | 15 | kg.cm/cm | |
| IZOD缺口冲击强度 | Notched 1/8" | ASTM D-256 | 18 | kg.cm/cm | |
| 洛氏硬度 | ASTM D-785 | 100 | R-scale | ||
| 热性能 | 热变形温度 | 18.5kg/cm21/2" | ASTM D-648 | 85 | ℃ |
| 维卡软化点 | 1000g | ASTM D-1525 | 93 | ℃ | |
| 阻燃等级 | 1/8" | UL94 | V-0 | ||