VydyneR228是一种40%矿物增强PA66树脂，其配方可提高冲击强度。可提供黑色，它是一种注塑级，旨在保留未增强PA66的固有加工优势，增强刚性、强度和耐热性。VydyneR228保持PA66对各种化学品、汽油、油、润滑脂和溶剂的典型耐化学性。
Vydyne R228 is a 40%mineral-reinforced PA66 resin formulated for improved impactstrength. Available in black, it is an injection-molding gradeformulated to retain the inherent processing advantages ofunreinforced PA66 while enhancing rigidity, strength and heatresistance. Vydyne R228 maintains the chemical resistance typicalof PA66 to a wide variety of chemicals, gasoline, oils, greases andsolvents
Vydyne R228树脂采用Ascend PerformanceMaterials开发的独特矿物增强PA66系统，以满足市场对高刚性热塑性塑料替代某些金属的需求。该矿物系统具有两个关键特征：
（1） 模塑件中各向同性行为特性的发展通常与流动方向无关。
(1) isotropicbehavior-property development in molded parts is usuallyindependent of flow direction.
（2） 减少了在大横截面（如模制的凸台和肋）中形成凹陷痕迹的趋势。
VydyneR228制成的零件不易下沉，但通常允许凸台和肋设计或壁横截面变化，这在其他非增强热塑性材料中是不可容忍的。VydyneR228树脂提供了更均匀的模塑零件强度和性能，以及更宽的零件设计自由度。
While not sink-free, partsmade from Vydyne R228 can often permit boss and rib design or wallcross section changes that would not be tolerable in otherunreinforced thermoplastic materials. Thus Vydyne R228 resin offersmore uniform molded part strength and performance, as well as widerlatitude in part design.
Vydyne R228树脂是Ascend PerformanceMaterials全系列矿物增强PA66树脂的主力，提供了较佳的财产总体平衡。VydyneR228是热稳定的，与未加固材料相比，其设计旨在提供更高的延展性和更低的熔体粘度。这种延展性的提高导致了更坚韧、更耐冲击的模制部件。熔体粘度的降低提高了注射成型的整体容易性，导致拉伸强度、模量和热变形温度的轻微降低。由VydyneR228制造的零件成功经受了烤漆炉循环，没有显著的尺寸稳定性或零件财产损
Vydyne R228 resin is aworkhorse of Ascend Performance Materials' full line ofmineral-reinforced PA66 resins, providing the best overall balanceof properties. Vydyne R228 is heat stabilized and designed toprovide increased ductility and reduced melt viscosity vs.unreinforced materials.This ductility improvement results intougher, more impact-resistant molded parts. The reduction in meltviscosity enhances overall ease of injection-molding, resulting inminor reductions in tensile strength, modulus and heat distortiontemperature. Parts manufactured from Vydyne R228 have successfullywithstood paint bake oven cycles without significant loss of eitherdimensional stability or part properties.
PA66注塑模工艺条件：
干燥处理：如果加工前材料是密封的，那么就没有必要干燥。如果储存容器被打开，那么建议在85℃的热空气中干燥处理。如果湿度大于0.2%，还需要进行105℃，12小时的真空干燥。
熔化温度：260~290℃。对玻璃添加剂的产品为275~280℃。熔化温度应避免高于300℃。
模具温度：建议80℃。模具温度将影响结晶度，而结晶度将影响产品的物理特性。对于薄壁塑件，如果使用低于40℃的模具温度，则塑件的结晶度将随着时间而变化，为了保持塑件的几何稳定性，需要进行退火处理。
注射压力：通常在750~1250bar，取决于材料和产品设计。
注射速度：高速（对于增强型材料应稍低一些）。
PA66用途：
①电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座、插座、接头、垫圈等；
②汽车：散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座、滤油器、变速杆等；
③工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑轮、电动工具等；
④其他：电动工具、护罩、风叶、齿轮、机床附件、运动器材、玩具制品、扎带等。