TOPAS®6013F-04
Cyclic Olefin Copolymer
Topas Advanced Polymers, Inc.
产品说明：
Product Description
TOPAS 6013F-04 is a high temperature, general purpose filmextrusion grade. It is a high clarity amorphous resin with highstiffness, moisture barrier, chemical resistance, thermoformabilityand purity for food and healthcare applications. It is used inmonolayer and blended cast applications, and in coextrusions andblends in both cast and blown processes, for a wide variety of filmand sheet products requiring excellent optics in applications suchas heat resistant blister, hot fill, and easy tear packaging. Ifperformance at elevated temperatures is not required, we also offerlower glass transition temperature (Tg) grades of TOPAS.
Selected Applications
Pharmaceutical blisters
Decorative film and sheet
General packaging
Food packaging
Healthcare and food contact
Leading Attributes
Clarity, forming, barrier, heat resistance, halogen-free
Gloss, hardness, chemical resistance, forming
Easy or linear tear, heat resistance, hot fill
Not manufactured with BPA, phthalates, or halogens
Broad regulatory compliance
Related Grades for Packaging and Film Extrusion
TOPAS 5013F-04 - high temperature grade with higher flow
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.02 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| 溶化体积流率（MVR） (230°C/2.16 kg) | 1.00 | cm³/10min | ISO 1133 |
| 吸水率 (饱和, 23°C) | 0.010 | % | ISO 62 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 70 | µm | |
| 拉伸模量 | ISO 527-3/1 | ||
| MD : 70 µm,铸造薄膜 | 2400 | MPa | ISO 527-3/1 |
| TD : 70 µm,铸造薄膜 | 2250 | MPa | ISO 527-3/1 |
| 拉伸应力 | ISO 527-3/50 | ||
| MD : 断裂, 70 µm,铸造薄膜 | 55.0 | MPa | ISO 527-3/50 |
| TD : 断裂, 70 µm,铸造薄膜 | 45.0 | MPa |