Polycarbonate (PC)
SABIC Innovative Plastics (GE Plastics)
产品说明：
Lexan* DMX9455 is a standard flow, flame retardant, V0/1.5mm,opaque polycarbonate copolymer resin with improved scratchresistance.
Thisdata was supplied by SABIC-IP for the Americas region.
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| 密度 | 1.17 g/cc | 0.0423 lb/in³ | ASTM D 792 |
| 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 | |
| 吸水率 | 0.080 % @Time 86400 sec | 0.080 % @Time 24.0 hour | ASTM D 570 |
| 平衡吸湿 | 0.13 % | 0.13 % | 23°C / 50% RH; ISO 62 |
| 0.13 % | 0.13 % | 50% RH; ASTM D 570 | |
| 0.28 % @Temperature 23.0 °C | 0.28 % @Temperature 73.4 °F | ASTM D 570 | |
| 0.040 % @Time 86400 sec | 0.040 % @Time 24.0 hour | 50% RH; ASTM D 570 | |
| 饱和吸水率 | 0.27 % @Temperature 23.0 °C | 0.27 % @Temperature 73.4 °F | ISO 62 |
| 线性成型收缩率,Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 13 g/10 min @Load 1.20 kg, Temperature 300 °C | 13 g/10 min @Load 2.65 lb, Temperature 572 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 14.5 g/10 min @Load 1.20 kg, Temperature 300 °C | 14.5 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D 1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Hardness, Rockwell L | 108 | 108 | ASTM D 785 |
| 洛氏硬度（M 级） | 93 | 93 | ASTM D 785 |
| 硬度，H358/30 | 128 MPa | 18600 psi | ISO 2039-1 |
| 抗张强度(断裂) | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 | |
| 抗张强度(屈服) | 80.0 MPa | 11600 psi | Type I, 50 mm/min; ASTM D 638 |
| 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | 40 % | 40 % | 50 mm/min; ISO 527 |
| 70 % | 70 % | Type I, 50 mm/min; ASTM D 638 | |
| 屈服伸长率 | 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D 638 |
| 7.0 % | 7.0 % | 50 mm/min; ISO 527 | |
| 拉伸模量 | 2.45 GPa | 355 ksi | 1 mm/min; ISO 527 |
| 2.90 GPa | 421 ksi | 50 mm/min; ASTM D 638 | |
| 弯曲强度 | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
| 120 MPa | 17400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 弯曲模量 | 2.45 GPa | 355 ksi | 2 mm/min; ISO 178 |
| 2.60 GPa | 377 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 悬壁梁缺口冲击强度 | 0.300 J/cm @Temperature 23.0 °C | 0.562 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| 0.300 J/cm @Temperature -30.0 °C | 0.562 ft-lb/in @Temperature -22.0 °F | ASTM D 256 | |
| 悬壁梁无缺口冲击强度 | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ASTM D 4812 |
| 悬壁梁缺口冲击强度 | 4.00 kJ/m² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | 80*10*3; ISO 180/1A |
| 5.00 kJ/m² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | 80*10*3; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | 45.0 kJ/m² @Temperature -30.0 °C | 21.4 ft-lb/in² @Temperature -22.0 °F | 80*10*3; ISO 180/1U |
| NB @Temperature 23.0 °C | 80*10*3; ISO 180/1U | ||
| 简支梁无缺口冲击强度 | 4.70 J/cm² @Temperature -30.0 °C | 22.4 ft-lb/in² @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature 23.0 °C | Edgew 80*10*3 sp=62mm; ISO 179/1eU | ||
| 简支梁缺口冲击强度 | 0.300 J/cm² @Temperature 23.0 °C | 1.43 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 0.300 J/cm² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 冲击试验 | 30.0 J @Temperature 23.0 °C | 22.1 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| Taber Abrasion, mg/1000 Cycles | 10 @Load 1.00 kg | 10 @Load 2.20 lb | CS-17; ASTM D 1044 |
| 10 @Load 1.00 kg | CS-17; SABIC Method |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 70.0 µm/m-°C @Temperature -40.0 - 95.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 203 °F | ASTM E 831 |
| 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 38.9 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | 70.0 µm/m-°C @Temperature -40.0 - 95.0 °C | ISO 11359-2 | |
| 比热容 | 1.40 J/g-°C | 0.335 BTU/lb-°F | ASTM C 351 |
| 导热系数 | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C 177 |
| 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ISO 8302 | |
| Hot Ball Pressure Test | <= 140 °C | <= 284 °F | IEC 60695-10-2 |
| 载荷下热变形温度(0.46 MPa) | 131 °C | 268 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 133 °C @Thickness 3.20 mm | 271 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| 载荷下热变形温度(1.8 MPa) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 119 °C @Thickness 3.20 mm | 246 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| 维卡软化温度 | 138 °C | 280 °F | Rate B/50; ISO 306 |
| 139 °C | 282 °F | Rate B/50; ASTM D 1525 | |
| 140 °C | 284 °F | Rate B/120; ISO 306 | |
| 可燃性(UL94) | V-2 @Thickness 1.00 mm | V-2 @Thickness 0.0394 in | UL 94 |
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL 94 |
| 材料描述 | 测试方法 | |
|---|---|---|
| 球压试验，125°C+/-2℃ | Passes | IEC 60695-10-2 |
| Erichson scratch depth, 6N, micrometer | 14 | SABIC Method |
| Pencil Hardness test, 1kgf | H | ASTM D 3363 |
LEXAN PC DMX9455特性与优点：
作为热塑性塑料，LEXAN聚碳酸酯树脂也叫lexan聚碳酸脂,是具特征的特殊化合物，避免了许多传统材料的缺陷。
一．强度：
LEXAN树脂显著的特征之一是高冲击强度。一般而言，没有其它的工程塑料能在极冷和极热的温度下承受得住猛烈撞击。
用LEXAN 树脂制成的产品通常防碎，几乎牢不可破。由于LEXAN树脂增加了强度，许多产品壁还可以制得更薄、重量更轻。
二．
LEXAN树脂不但强度高，还具有下列特性：抗热(高达100°C)，抗冷(低达零下40°C)，抗水，抗老化，抗紫外线，抗火焰。
三．外观：
GE塑料的LEXAN树脂使今天杰出产品设计的许多视觉特征成为可能。从几乎无限的颜色和色调，生动的表面质地、
水晶般晶莹透明或半透明、金属片、斑点或散布的特殊效果。
四．光学纯度：
LEXAN树脂不只表面漂亮，同时具有高纯度、杰出的透明性和一致的质量。LEXAN 0Q树脂被广泛用于满足CD、DVD和光媒体的高标准，
改变我们目前欣赏视频、享受音乐和获取信息的方式。其光学特征同样有助于制成更结实、更薄、更轻的眼镜，
从而保护我们的工作和游戏方式。
五．电兼容性，因为阻燃剂范围广，可在众多电子产品中发现LEXAN树脂，包括家庭和个人护理用品、仪表和保险盒、开关、
插头和插座等...................