SABICInnovative Plastics Lexan® 953A PC (Asia Pacific)
Polycarbonate (PC)
SABIC Innovative Plastics (GE Plastics)
产品说明：
Clear, tints and opaque colors, high viscosity, flame retardantwith exceptional surface. UV-stabilized.
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| 密度 | 1.217 g/cc | 0.04397 lb/in³ | ASTM D792 |
| 吸水率 | 0.15 % @Time 86400 sec | 0.15 % @Time 24.0 hour | ASTM D570 |
| 平衡吸湿 | 0.35 % | 0.35 % | ASTM D570 |
| 0.58 % @Temperature 100 °C | 0.58 % @Temperature 212 °F | ASTM D570 | |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 7.0 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | 70 | 70 | ASTM D785 |
| 洛氏硬度（R 级） | 118 | 118 | ASTM D785 |
| 抗张强度(断裂) | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| 抗张强度(屈服) | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 90 % | 90 % | Type I, 50 mm/min; ASTM D638 |
| 屈服伸长率 | 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D638 |
| 弯曲强度 | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 弯曲模量 | 2.24 GPa | 325 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 悬壁梁缺口冲击强度 | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 |
| 悬壁梁无缺口冲击强度 | 32.04 J/cm | 60.02 ft-lb/in | ASTM D4812 |
| 拉伸冲击强度 | 525 kJ/m² | 250 ft-lb/in² | Type S; ASTM D1822 |
| 落锤总能量 | 169 J | 125 ft-lb | ASTM D3029 |
| 泰伯磨损，毫克/1000次 | 10 | 10 | CS-17, 1 kg; ASTM D1044 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | ASTM D257 |
| 介电常数 | 2.96 @Frequency 1.00e+6 Hz | 2.96 @Frequency 1.00e+6 Hz | ASTM D150 |
| 3.01 @Frequency 50.0 - 60.0 Hz | 3.01 @Frequency 50.0 - 60.0 Hz | ASTM D150 | |
| 介电强度 | 16.7 kV/mm @Thickness 3.20 mm | 424 kV/in @Thickness 0.126 in | in air; ASTM D149 |
| 耗散因数 | 0.00090 @Frequency 50.0 - 60.0 Hz | 0.00090 @Frequency 50.0 - 60.0 Hz | ASTM D150 |
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | ASTM D150 | |
| 耐电弧性 | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
| 相比耐漏电起痕指数(CTI) | 175 - 250 V | 175 - 250 V | UL 746A |
| 热丝引燃 (HWI) | 30 - 60 sec | 30 - 60 sec | UL 746A |
| 高电弧燃烧，HAI | 30 - 60 arcs | 30 - 60 arcs | UL 746A |
| 高压电弧跟踪率，HVTR | 80.0 - 150 mm/min | **** - 5.91 in/min | UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 68.4 µm/m-°C @Temperature -40.0 - 95.0 °C | 38.0 µin/in-°F @Temperature -40.0 - 203 °F | ASTM E 831 |
| 导热系数 | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | ASTM C177 |
| 载荷下热变形温度(0.46 MPa) | 137 °C @Thickness 6.40 mm | 279 °F @Thickness 0.252 in | unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 132 °C @Thickness 6.40 mm | 270 °F @Thickness 0.252 in | unannealed; ASTM D648 |
| 维卡软化温度 | 151 °C | 304 °F | Rate B/50; ASTM D1525 |
| UL RTI | 130 °C | 266 °F | UL 746B |
| UL RTI，机械冲击 | 120 °C | 248 °F | UL 746B |
| UL RTI，机械无冲击 | 130 °C | 266 °F | UL 746B |
| 可燃性(UL94) | V-2 @Thickness 1.47 mm | V-2 @Thickness 0.0579 in | UL 94 |
| V-0 @Thickness 2.99 mm | V-0 @Thickness 0.118 in | UL 94 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 折射率 | 1.586 | 1.586 | ASTM D542 |
| 雾度 | 1.0 % @Thickness 2.54 mm | 1.0 % @Thickness 0.100 in | ASTM D1003 |
| Transmission, Visible | 85 % | 85 % | 2.54 mm; ASTM D1003 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Specific Volume | 0.83cm^3/g | ASTM D792 |
| UV-light, water exposure/immersion | F1 | UL 746C |
塑料是只有几十年的历史，但在这短短的时间，他们已经成为建立在我们生活的每一个领域。它有一个巨大的潜力，促进可持续发展发展。PC塑料的结构单元主要来自石油和天然气生产。高分子化学在短短几十年彻底改变了世界的工程材料,PC材料有许多优点，特别是从环境的观点。与其它材料相比，它们需要很少能源的生产和加工。他们将继续增长，在全球范围内为我们解决当前和未来的挑战，确保我们的生活水平和生活质量。这些PC原料主要在建筑，汽车，电气和电子，纺织，包装，家具等行业得以高效应用。PC塑料的不同性能也越来越有吸引力从其他行业的客户。通过代以用于其他材料，以可持续的方式生产过程中节约更多资源，生产更多的能源效率，使用更经济有效的原料。高油耗汽车不再是一个不可避免的功能：约一半的燃油消耗的重量取决于车辆的塑料减少重量，这样有利于节约能源并减少废气排放