代理 基础创新塑料(美国) 耐水解 PC LEXAN™ EXL1414 resin 共聚物

LEXAN™ EXL1414 resin

Polycarbonate

SABIC Innovative Plastics

产品说明：

LEXAN EXL1414 polycarbonate (PC) siloxane copolymer resin is amedium flow opaque injection molding (IM) grade. This resin offersextreme low temperature (-40 C) ductility in combination withexcellent processability and release with opportunities for shorterIM cycle times compared to standard PC. LEXAN EXL1414 resin is aproduct available in wide range of opaque colors and may be anexcellent candidate for a wide variety of applications.

物性信息：

基本信息
特性

共聚物

可加工性，良好

快的成型周期

流动性中等

通用

脱模性能良好

延展性

用途

通用

外观

不透明

可用颜色

加工方法

注射成型

多点数据

Coefficient of Thermal Expansion vs. Temperature (ASTM E831)

Flexural DMA (ASTM D4065)

Pressure-Volume-Temperature (PVT - Zoller Method)

Shear DMA (ASTM D4065)

Specific Heat vs. Temperature (ASTM D3417)

Tensile Fatigue

Tensile Stress vs. Strain (ASTM D638)

Thermal Conductivity vs. Temperature (ASTM E1530)

Viscosity vs. Shear Rate (ASTM D3835)

物理性能额定值单位制测试方法比重


    --1.18g/cm³ASTMD792    --1.19g/cm³ISO 1183熔流率（熔体流动速率） (300°C/1.2 kg)10g/10 minASTMD1238溶化体积流率（MVR） (300°C/1.2kg)9.00cm³/10minISO 1133收缩率

内部方法    流动 : 3.20mm0.40 到 0.80%内部方法    横向流动 : 3.20 mm0.40 到 0.80%内部方法吸水率

ISO 62    饱和,23°C0.35%ISO 62    平衡, 23°C, 50% RH0.15%ISO 62硬度额定值单位制测试方法洛氏硬度

ASTM D785    L计秤89
ASTM D785    R级121
ASTM D785机械性能额定值单位制测试方法拉伸模量


    -- 12020MPaASTMD638    --2150MPaISO 527-2/1抗张强度


    屈服 255.5MPaASTMD638    屈服57.0MPaISO527-2/50    断裂 350.3MPaASTMD638    断裂60.0MPaISO 527-2/50伸长率


    屈服 46.0%ASTMD638    屈服6.0%ISO527-2/50    断裂 598%ASTMD638    断裂120%ISO527-2/50弯曲模量


    50.0 mm跨距 62230MPaASTMD790    -- 72250MPaISO 178弯曲应力


    --85.0MPaISO178    屈服, 50.0 mm跨距 892.4MPaASTMD790冲击性能额定值单位制测试方法简支梁缺口冲击强度 9

ISO 179/1eA    -30°C65kJ/m²ISO179/1eA    23°C70kJ/m²ISO179/1eA简支梁无缺口冲击强度 10

ISO 179/1eU    -30°C无断裂
ISO 179/1eU    23°C无断裂
ISO 179/1eU悬壁梁缺口冲击强度


    -30°C770J/mASTMD256    23°C870J/mASTMD256    -30°C 1160kJ/m²ISO180/1A    23°C 1270kJ/m²ISO180/1A无缺口伊佐德冲击强度 13

ISO 180/1U    -30°C无断裂
ISO 180/1U    23°C无断裂
ISO 180/1U装有测量仪表的落镖冲击 (23°C, TotalEnergy)70.0JASTM D3763热性能额定值单位制测试方法载荷下热变形温度


    0.45 MPa, 未退火, 3.20mm139°CASTM D648    0.45 MPa, 未退火, 100 mm跨距 14140°CISO75-2/Be    1.8 MPa, 未退火,3.20 mm124°CASTM D648    1.8 MPa, 未退火, 100 mm跨距 15128°CISO 75-2/Ae维卡软化温度


    --145°CASTMD1525, ISO306/B50 11 16    --146°CISO306/B120Ball Pressure Test (125°C)Pass
IEC 60695-10-2线形热膨胀系数


    流动 : -40 到40°C7.0E-5cm/cm/°CASTME831    流动 : 23 到80°C7.2E-5cm/cm/°CISO11359-2    横向 : -40 到40°C7.5E-5cm/cm/°CASTME831    横向 : 23 到80°C7.2E-5cm/cm/°CISO 11359-2RTI Elec130°CUL 746RTIImp120°CUL 746RTI125°CUL 746电气性能额定值单位制测试方法表面电阻率> 1.0E+15ohmsASTMD257体积电阻率> 1.0E+15ohms·cmASTM D257介电强度 (0.800 mm, in Oil)16kV/mmASTM D149介电常数

ASTM D150    100Hz2.68
ASTM D150    1MHz2.64
ASTM D150耗散因数

ASTM D150    100Hz1.2E-3
ASTM D150    1MHz9.3E-3
ASTM D150可燃性额定值单位制测试方法UL 阻燃等级 (0.400mm)HB
UL 94灼热丝易燃指数

IEC 60695-2-12    0.800mm850°CIEC 60695-2-12    1.00 mm960°CIEC 60695-2-12热灯丝点火温度

IEC 60695-2-13    1.00mm875°CIEC 60695-2-13    3.00 mm875°CIEC 60695-2-13注射额定值单位制
干燥温度121°C
干燥时间3.0 到 4.0hr
干燥时间，*大48hr
建议的*大水分含量0.020%
建议注射量40 到 60%
料筒后部温度217 到 293°C
料筒中部温度282 到 304°C
料筒前部温度293 到 316°C
射嘴温度288 到 310°C
加工（熔体）温度293 到 316°C
模具温度71.0 到 93.0°C
背压0.345 到 0.689MPa
螺杆转速40 到 70rpm
排气孔深度0.025 到 0.076mm
备注1 .50 mm/min2 .类型 1, 50 mm/min3 .类型 1, 50 mm/min4 .类型 1, 50mm/min5 .类型 1, 50 mm/min6 .1.3 mm/min7 .2.0 mm/min8 .1.3 mm/min9.80*10*3 sp=62mm10 .80*10*3 sp=62mm11 .80*10*312 .80*10*313.80*10*314 .120*10*4 mm15 .120*10*4 mm16 .标准 B (120°C/h), 载荷2 (50N)

lexan PCEXL1414T聚碳酸酯（PC）硅氧烷共聚物树脂是一种透明的注塑级树脂。该树脂具有极低的温度（-40°C）延展性，具有中等的流动特性和良好的加工性能，与标准PC相比，有机会缩短IM循环时间。LexanExl1414T树脂是一种通用产品，具有透明和不透明的颜色，是广泛应用的**候选材料

PC(Polycarbonate Polymer)比广泛使用的塑料更硬、更轻，

是用作工业材料高功能性塑料“工程塑料”中的一种。 

聚碳酸脂也是防弹玻璃的材料，具有耐冲击性、耐热性、透明性等特性，

被广泛用于电子、汽车、机械零件等各种领域。

lexan PCEXL1414T聚碳酸酯是一种非晶态聚合物，具有独特的韧性和冲击强度。它还表现出高光学清晰度，优良的蠕变和耐高温性。

lexan PC EXL1414T主要优点

1、具高强度及弹性系数、高冲击强度、使用温度范围广;

2、高度透明性及自由染色性;

3、成形收缩率低、尺寸安定性良好；

4、耐疲劳性佳;

5、耐候性佳;

6、电气特性优;

7、无味无臭对人体无害符合卫生安全

PC工程塑料的三大应用领域是玻璃装配业、汽车工业和电子、电器工业，还有工业机械零件、光盘、包装、计算机等办公室设备、医疗及保健、薄膜、休闲和防护器材等。PC可用作门窗玻璃，PC层压板广泛用于银行、使馆、拘留所和公共场所的防护窗，用于飞机舱罩，照明设备、工业安全档板和防弹玻璃。