德固赛PA12 CX9710耐磨PA抗UVDescription: TROGAMID® CX compoundsround off the product range of High Performance Polymers to includesemicrystalline polyamides, the crystallites of which are so smallthat they do not scatter visible light—a property known asmicrocrystallinity. The compounds are therefore as clear as glass.They possess higher resistance to chemicals and stress crackingthan amorphous transparent plastics, in addition to the mechanicaladvantages of amorphous compounds. The outstanding properties ofTROGAMID® CX are:
crystal-clear, permanent transparency; high transmission
superior chemical and stress cracking resistance
high level of UV resistance
low water absorption, which leaves the mechanical propertiesvirtually unaffected
high dimensional stability
balanced mechanical property profile
high impact resistance, even at low temperatures
high level of dynamic strength (e.g., for internally pressurizedparts)
abrasion and scratch resistance
high glass transition temperature
very low isotropic shrinkage
easy processing
The unique combination of properties in TROGAMID® CX compoundspermits their use over a broad application spectrum. Areas ofapplication can be as diverse as water management, filtertechnology, laboratory and medical technology, the manufacture ofeyeglasses, or bottles for the cosmetics industry.
Specific Notes for this Material: Medium-viscous, permanentlytransparent polyamide for injection molding and extrusion, with aninternal mold release agent
Information provided by degussa.
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
| Melt Density | 0.900 g/cc | 0.0325 lb/in³ | |
| 粘度测试 | >= 150 cm³/g | >= 150 cm³/g | Viscosity Number; ISO 307 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 80 | 80 | ISO 868 |
| 球压硬度 | 110 MPa | 16000 psi | H30; ISO 2039-1 |
| 抗张强度(断裂) | >= 50.0 MPa | >= 7250 psi | 50 mm/min; ISO 527-1/2 |
| 抗张强度(屈服) | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527-1/2 |
| 伸长率 (断裂) | >= 150 % | >= 150 % | 50 mm/min; ISO 527-1/2 |
| 屈服伸长率 | 8.0 % | 8.0 % | 50 mm/min; ISO 527-1/2 |
| 9.0 % | 9.0 % | 5 mm/min, Outer fiber strain at maximum stress; ISO 178 |