北欧化工HDPE HE6062耐磨HDPE---Borstar HE6062 is a black high density(HD) jacketing compound, which is produced with the Borealisproprietary
Borstar bimodal process technology.
Borstar technology allows the manufacturing of polymers outside thetraditional MFR and density range making it possible to optimizeprocessability, reduce shrinkage and yet provide excellent physicaltoughness and environmental stress crack resistance (ESCR).
Borstar HE6062 contains 2.5% well-dispersed carbon black in orderto ensure excellent weathering resistance.
BorStar® HDPE HE6062 >HDPE-CB2.5<
熔融指数: 0.5 g/10min
邵氏硬度D: 61
加工方式: 挤出成型
材料属性: 2.5%炭黑 填充 耐热级 抗UV级 耐磨级
符合规定: ASTM D 1248 Type III,Class C,Category 4,GradeE8,E9,J4,W8,9 • DIN VDE 0207 Type 2YM3 • DIN VDE 0818 • EN 187105 •EN 50290-2-24 • HD 603 S1,DMP 1,2,5,7,8 • HD 620 S2,Part 1,table4B,DMP 2,8-12,14-15,17 • HD 632 S2,ST7 • IEC 60502-2 Type ST7
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | ISO 1183 | ||
| -- 1 | 0.946 | g/cm³ | ISO 1183 |
| -- 2 | 0.958 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） | ISO 1133 | ||
| 190°C/2.16kg | 0.50 | g/10 min | ISO 1133 |
| 190°C/5.0kg | 2.0 | g/10 min | ISO 1133 |
| 抗环境应力开裂 3(条件B, 50°C, 10% Igepal, F0) | > 5000 | hr | IEC 60811-4-1/B |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 | |||
| 邵氏 D, 1 秒 | 61 | ISO 868 | |
| 邵氏 D, 3 秒 | 60 | DIN 53505 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力 (屈服) | 33.0 | MPa | ISO 527-2/50 |
| 拉伸应变 (断裂) | 1000 | % | ISO 527-2/50 |
| 弯曲模量 | 1000 | MPa | ASTM D790 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 脆化温度 | < -76.0 | °C | ASTM D746 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.0E+16 | ohms·cm | IEC 60093 |
| 介电强度 | 20 | kV/mm | IEC 60243-1 |