原包日本宝理40%玻矿LCP LAPEROS E463i
Density | 1.72 | g/cm³ | ISO 1183 |
Molding Shrinkage 3 | Internal Method | ||
Across Flow : 1.00 mm | 0.50 | % | |
Flow : 1.00 mm | 0.090 | ||
Water Absorption (24 hr, 23°C) | 0.020 | ISO 62 | |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness (M-Scale) | 45 | ISO 2039-2 |
| Mechanical | Nominal Value | ||
Tensile Strength | 110 | MPa | ASTM D638 |
Tensile Elongation (Break) | 3.0 | ASTM D638 | |
Flexural Modulus | 10600 | ISO 178 | |
Flexural Stress | 130 | ISO 178 | |
Flexural Strain | 3.1 | ISO 178 | |
| Impact | Nominal Value | ||
Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | ||
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 270 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 235 | ISO 75-2/A |
| Electrical | Nominal Value | ||
Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
Electric Strength | IEC 60243-1 | ||
1.00 mm | 44 | kV/mm | |
3.00 mm | 22 | ||
Relative Permittivity | IEC 60250 | ||
1 kHz | 4.50 | ||
1 MHz | 3.90 | ||
Dissipation Factor | 0.030 | ||
Arc Resistance | 182 | sec | ASTM D495 |
Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | ||
Flame Rating | V-0 | UL 94 |
LCP还可以做印刷电路板、人造卫星电子部件、喷气发动机零件；用于电子电气和汽车机械零件或部件；还可以用于医疗方面。4）LCP塑胶原料可以加入高填充剂作为集成电路封装材料，以代替环氧树脂作线圈骨架的封装材料；作光纤电缆接头护套和高强度元件；代替陶瓷作化工用分离塔中的填充材料等。5）LCP塑胶原料还可以与聚砜、PBT、聚酰胺等塑料共混制成合金，制件成型后其机械强度高，用以代替玻璃纤维增强的聚砜等塑料，既可提高机械强度性能，又可提高使用强度及化学稳定性等。目前正在研究将LCP用于宇航器外部的面板、汽车外装的制动系统等。