低摩擦 PA66 德国DOMO 66Y10道默尼龙 润滑性 低摩擦 PA66德国DOMO 66Y10道默尼龙 润滑性 低摩擦 PA66 德国DOMO 66Y10道默尼龙润滑性
度 | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU |
NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
简支梁缺口冲击强度 | 0.540 J/cm2 @Temperature -30.0 °C | 2.57 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
0.540 J/cm2 @Temperature 23.0 °C | 2.57 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
体积电阻率 | 1.00e 11 ohm-cm @Thickness 0.750 mm | 1.00e 11 ohm-cm @Thickness 0.0295 in | IEC 60093 |
介电强度 | 13.0 kV/mm @Thickness 1.00 mm | 330 kV/in @Thickness 0.0394 in | IEC 60243 |
耐电弧性 | 120 - 179 sec @Thickness 3.00 mm | 120 - 179 sec @Thickness 0.118 in | ASTM D495 |
相比耐漏电起痕指数(CTI) | 600 V @Thickness 3.00 mm | 600 V @Thickness 0.118 in | IEC 60112 |
热丝引燃 (HWI) | 7.0 - 14 sec @Thickness 0.400 mm | 7.0 - 14 sec @Thickness 0.0157 in | UL 746 |
7.0 - 14 sec @Thickness 0.750 mm | 7.0 - 14 sec @Thickness 0.0295 in | UL 746 | |
7.0 - 14 sec @Thickness 1.50 mm | 7.0 - 14 sec @Thickness 0.0591 in | UL 746 | |
15 - 29 sec @Thickness 3.00 mm | 15 - 29 sec @Thickness 0.118 in | UL 746 | |
高电弧燃烧指数(HAI) | >= 120 arcs @Thickness 0.400 mm | >= 120 arcs @Thickness 0.0157 in | UL 746 |
>= 120 arcs @Thickness 0.750 mm | >= 120 arcs @Thickness 0.0295 in | UL 746 | |
>= 120 arcs @Thickness 1.50 mm | >= 120 arcs @Thickness 0.0591 in | UL 746 | |
>= 120 arcs @Thickness 3.00 mm | >= 120 arcs @Thickness 0.118 in | UL 746 | |
高压电弧跟踪率,HVTR | 10.1 - 25.4 mm/min | 0.398 - 1.00 in/min | UL 746 |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
线形热膨胀系数 - 流动 | 11.0 μm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 6.11 μin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359-2 |
线性热膨胀系数,横向流动 | 11.0 μm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | ISO 11359-2 | |
熔融温度 | 244 °C | 471 °F | ISO 11357-3 |
载荷下热变形温度(0.46 MPa) | 225 °C | 437 °F | Unannealed; ISO 75-2/B |
载荷下热变形温度(1.8 MPa) | 65.0 °C | 149 °F | Unannealed; ISO 75-2/A |
UL RTI | 130 °C @Thickness 0.400 mm | 266 °F @Thickness 0.0157 in | UL 746 |
130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL 746 | |
130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746 | |
130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746 | |
UL RTI,机械冲击 | 65.0 °C @Thickness 0.400 mm | 149 °F @Thickness 0.0157 in | UL 746 |
65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | UL 746 | |
85.0 °C @Thickness 1.50 mm | 185 °F @Thickness 0.0591 in | UL 746 | |
85.0 °C @Thickness 3.00 mm | 185 °F @Thickness 0.118 in | UL 746 | |
UL RTI,机械无冲击 | 100 °C @Thickness 0.400 mm | 212 °F @Thickness 0.0157 in | UL 746 |
100 °C @Thickness 0.750 mm | 212 °F @Thickness 0.0295 in | UL 746 | |
100 °C @Thickness 1.50 mm | 212 °F @Thickness 0.0591 in | UL 746 | |
110 °C @Thickness 3.00 mm | 230 °F @Thickness 0.118 in | UL 746 | |
可燃性(UL94) | V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | |
V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | ||
V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||
V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||
极限氧指数 | 29 % | 29 % | ISO 4589-2 |
灼热丝易燃指数 | 725 °C @Thickness 3.00 mm | 1340 °F @Thickness 0.118 in | Ignition Temperature; IEC 60695-2-13 |
775 °C @Thickness 1.50 mm | 1430 °F @Thickness 0.0591 in | Ignition Temperature; IEC 60695-2-13 | |
875 °C @Thickness 0.400 mm | 1610 °F @Thickness 0.0157 in | Ignition Temperature; IEC 60695-2-13 | |
875 °C @Thickness 0.750 mm | 1610 °F @Thickness 0.0295 in | Ignition Temperature; IEC 60695-2-13 | |
960 °C @Thickness 0.400 mm | 1760 °F @Thickness 0.0157 in | Flammability Index; IEC 60695-2-12 | |
960 °C @Thickness 0.750 mm | 1760 °F @Thickness 0.0295 in | Flammability Index; IEC 60695-2-12 | |
960 °C @Thickness 1.50 mm | 1760 °F @Thickness 0.0591 in | Flammability Index; IEC 60695-2-12 | |
960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | Flammability Index; IEC 60695-2-12 |
加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
料筒后部温度 | 240 - 270 °C | 464 - 518 °F | |
料筒中部温度 | 240 - 270 °C | 464 - 518 °F | |
料筒前部温度 | 240 - 270 °C | 464 - 518 °F | |
射嘴温度 | 240 - 270 °C | 464 - 518 °F | |
加工(熔体)温度 |