SABIC InnovativePlastics Lexan®DMX9455 PC共聚物聚碳酸酯（PC）热塑性聚合物SABIC Innovative Plastics（通用电气塑料公司）产品说明:Lexan*DMX9455是一种标准流动、阻燃、V0/1.5mm、不透明的聚碳酸酯共聚物树脂，具有更好的抗划伤性。该数据由SABIC-IP提供给美洲地区。
SABIC Innovative Plastics Lexan® DMX9455 PC Copolymer 物性表
基础创新塑料PC DMX9455，阻燃PC
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| 密度 | 1.17 g/cc | 0.0423 lb/in³ | ASTM D 792 |
| 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 | |
| 吸水率 | 0.080 % @Time 86400 sec | 0.080 % @Time 24.0 hour | ASTM D 570 |
| 平衡吸湿 | 0.13 % | 0.13 % | 23°C / 50% RH; ISO 62 |
| 0.13 % | 0.13 % | 50% RH; ASTM D 570 | |
| 0.28 % @Temperature 23.0 °C | 0.28 % @Temperature 73.4 °F | ASTM D 570 | |
| 0.040 % @Time 86400 sec | 0.040 % @Time 24.0 hour | 50% RH; ASTM D 570 | |
| 饱和吸水率 | 0.27 % @Temperature 23.0 °C | 0.27 % @Temperature 73.4 °F | ISO 62 |
| 线性成型收缩率,Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 13 g/10 min @Load 1.20 kg, Temperature 300 °C | 13 g/10 min @Load 2.65 lb, Temperature 572 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 14.5 g/10 min @Load 1.20 kg, Temperature 300 °C | 14.5 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D 1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Hardness, Rockwell L | 108 | 108 | ASTM D 785 |
| 洛氏硬度（M 级） | 93 | 93 | ASTM D 785 |
| 硬度，H358/30 | 128 MPa | 18600 psi | ISO 2039-1 |
| 抗张强度(断裂) | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 | |
| 抗张强度(屈服) | 80.0 MPa | 11600 psi | Type I, 50 mm/min; ASTM D 638 |
| 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | 40 % | 40 % | 50 mm/min; ISO 527 |
| 70 % | 70 % | Type I, 50 mm/min; ASTM D 638 | |
| 屈服伸长率 | 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D 638 |
| 7.0 % | 7.0 % | 50 mm/min; ISO 527 | |
| 拉伸模量 | 2.45 GPa | 355 ksi | 1 mm/min; ISO 527 |
| 2.90 GPa | 421 ksi | 50 mm/min; ASTM D 638 | |
| 弯曲强度 | 108 MPa | 15700 psi | 2 mm/min; ISO 178 |
| 120 MPa | 17400 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 弯曲模量 | 2.45 GPa | 355 ksi | 2 mm/min; ISO 178 |
| 2.60 GPa | 377 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 悬壁梁缺口冲击强度 | 0.300 J/cm @Temperature 23.0 °C | 0.562 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| 0.300 J/cm @Temperature -30.0 °C | 0.562 ft-lb/in @Temperature -22.0 °F | ASTM D 256 | |
| 悬壁梁无缺口冲击强度 | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ASTM D 4812 |
| 悬壁梁缺口冲击强度 | 4.00 kJ/m² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | 80*10*3; ISO 180/1A |
| 5.00 kJ/m² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | 80*10*3; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | 45.0 kJ/m² @Temperature -30.0 °C | 21.4 ft-lb/in² @Temperature -22.0 °F | 80*10*3; ISO 180/1U |
| NB @Temperature 23.0 °C | 80*10*3; ISO 180/1U | ||
| 简支梁无缺口冲击强度 | 4.70 J/cm² @Temperature -30.0 °C | 22.4 ft-lb/in² @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature 23.0 °C | Edgew 80*10*3 sp=62mm; ISO 179/1eU | ||
| 简支梁缺口冲击强度 | 0.300 J/cm² @Temperature 23.0 °C | 1.43 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 0.300 J/cm² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 冲击试验 | 30.0 J @Temperature 23.0 °C | 22.1 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| Taber Abrasion, mg/1000 Cycles | 10 @Load 1.00 kg | 10 @Load 2.20 lb | CS-17; ASTM D 1044 |
| 10 @Load 1.00 kg | CS-17; SABIC Method |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 70.0 µm/m-°C @Temperature -40.0 - 95.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 203 °F | ASTM E 831 |
| 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 38.9 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| 线性热膨胀系数,横向流动 | 70.0 µm/m-°C @Temperature -40.0 - 95.0 °C | ISO 11359-2 | |
| 比热容 | 1.40 J/g-°C | 0.335 BTU/lb-°F | ASTM C 351 |
| 导热系数 | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C 177 |
| 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ISO 8302 | |
| Hot Ball Pressure Test | <= 140 °C | <= 284 °F | IEC 60695-10-2 |
| 载荷下热变形温度(0.46 MPa) | 131 °C | 268 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 133 °C @Thickness 3.20 mm | 271 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| 载荷下热变形温度(1.8 MPa) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 119 °C @Thickness 3.20 mm | 246 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| 维卡软化温度 | 138 °C | 280 °F | Rate B/50; ISO 306 |
| 139 °C | 282 °F | Rate B/50; ASTM D 1525 | |
| 140 °C | 284 °F | Rate B/120; ISO 306 | |
| 可燃性(UL94) | V-2 @Thickness 1.00 mm | V-2 @Thickness 0.0394 in | UL 94 |
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL 94 |
| 材料描述 | 测试方法 | |
|---|---|---|
| 球压试验，125°C+/-2℃ | Passes | IEC 60695-10-2 |
| Erichson scratch depth, 6N, micrometer | 14 | SABIC Method |
| Pencil Hardness test, 1kgf | H | ASTM D 3363 |
基础创新塑料PC DMX9455，阻燃PC
SABIC-LEXAN-PC塑料材料
SABIC-LEXAN-PC所有牌号列表
>
pc（聚碳酸酯(Polycarbonate 简称PC)）一般指聚碳酸酯
聚碳酸酯(简称PC)是分子链中含有碳酸酯基的高分子聚合物，根据酯基的结构可分为脂肪族、芳香族、脂肪族-芳香族等多种类型。其中由于脂肪族和脂肪族-芳香族聚碳酸酯的机械性能较低，从而限制了其在工程塑料方面的应用。目前仅有芳香族聚碳酸酯获得了工业化生产。由于聚碳酸酯结构上的特殊性，现已成为五大工程塑料中增长速度快的通用工程塑料。
| 商标 | 形态 | 型号 | 简要说明 | |
| SABIC PC | 透明PC | 4800 | 48融指，光盘料 | |
| 1000R | 易脱模，注塑成型，广泛用途 | |||
| 1800R | ||||
| 2200R | ||||
| 1003R | 易脱模，抗UV，注塑成型，用于电表、镜片等行业 | |||
| 0703R | 7融指，易脱模，抗UV，尤其适用于挤出板材、灯管，也可用于注塑成型 | |||
| LEXAN PC | 透明PC | PK2870 | 2.5融指，食品级，尤其适用于吹塑成型 | |
| 103R | 7融指，易脱模，抗UV，尤其适用于挤出板材、灯管，也可用于注塑成型 | |||
| 141R 143R 144R 121R 123R 124R | 融指10，HB级别，普通PC，耐候/FDA，多种注塑用途 | |||
| 241R 243R 244R 221R 223R 224R | 融指10，3mm防火V2，6mm V0，耐候/FDA，多种注塑用途 | |||
| HF1110 HF1130 HF1140 | 融指25，1-1.5mm防火V2，耐候/FDA，多种注塑用途 | |||
| 950A 953A 955A 955AU 940A 943A 945A 945AU 920A 923A 925A 925AU | 融指7-15，3mm防火V0，耐候/FDA/无卤阻燃，多种注塑用途 | |||
| 不透防火 | 950 953 955 955U 940 943 945 945U 920 923 925 925U | 融指7-15，1-1.5mm防火V0，耐候/FDA/无卤阻燃，多种注塑用途 | ||
| 玻纤增强 | 500R 503R 505R 505RU 3412R 3413R 3414R | 10%-40%玻纤增强，1.5mm防火V0 | ||
| 低温超韧 | EXL1112 EXL1414 EXL1434 EXL9330 | 耐低温-20至-60℃，防火等级可选，广泛用于手机及小家电领域,透明/不透明 | ||
| 超级耐候 | SLX2432 SLX1432 SLX5432SLX6434 | 多种选择：透明/不透明，防火/不防火 | ||
| 耐热透明 | 4401R 4501R 4701R XHT1141 XHT2141 XHT3141 XHT4141 | 热变形温度140-170℃，耐候/FDA，多种注塑用途，HB级别 | ||
| 医疗专用 | HP1 HP2 HP4 | ETO消毒专用，融指10-25 | ||
| HPS1 HPS2 HPS4 | 伽马射线消毒专用，融指10-25 | |||
| 汽车照明 | LS1 LS2 LS3 | 耐候F1，融指7-25 | ||
| 眼镜专用 | OQ4120 OOQ4620 OQ4820 | 太阳镜专用，UV 400nm阻隔，融指6-25 | ||
| OQ3120 OOQ3420 OQ3820 | 眼科380nm临界值，融指6-25 | |||
| LED专用 | LUX系列 | 2010T 2180T 9130C 7430C 9610 7630C | 透明，融指40-5,多种耐候及防火等级选择; 0.75mm V2 -3mm5VA/1.2mm V0-1.0mm V0 | |
| 2114 9132C 9136C 9612 9616 7432C | 不透明，多种光扩散程度选择，融指18-7，多种耐候及防火等级选择 | |||
| 高反射 | 915R-WH9G002 | 不透明，融指18, 1.1mm V0, RTI≥120℃ | ||
| BFL2000 BFL2010 BFL2015 BFL4000U | 高流动性/高反射率，0%-20%玻纤增强, 1.5mm防火V0， | |||
基础创新塑料PC DMX9455，阻燃PC
PC在耐冲击性、耐热性、尺寸稳定性、电学特性、透明性以及卫生性能等诸多方面具有其突出的优点。现被广泛应用于电子电器、办公用品、精密机械、汽车、医疗、安保及家庭用品等众多领域。
pc是具有以下分子结构的热塑性树脂，可采用注塑、挤塑、吹塑等成型方式进行加工。
耐冲击性
在塑料中具有高的耐冲击强度值，且该特性高于铸锌和铸铝。
使用温度范围
在低温到高温很宽的范围内仍可保持稳定的特性。
电学特性
在很宽的温度范围内使用时变化很小，可作为优良的绝缘材料。
透明性
具有塑料中少有的优异透明性，适合光学及板材用途。
尺寸稳定性
具有优良的耐蠕变性能，尺寸几乎不受吸湿、温度、时间变化的影响。
阻燃性
具有优良的阻燃性，通过了UL规格Subject94的V-0、V-1、V-2、HB、5VA、5VB等级测试。
PC中文名称聚碳酸酯，系非结晶性热塑性工程塑料。
优点：
1、具高强度及弹性系数、高冲击强度、使用温度范围广；2、高度透明性及自由染色性；3、H.D.T.高；4、耐疲劳性佳；5、耐候性佳；6、电气特性优；7、无味无臭对人体无害符合卫生安全；8、成形收缩率低、尺寸安定性良好。
用途：
1、电子电器：CD片、开关、家电外壳、信号筒、电容器、电话机壳体、电话交换器、信号继电器及零件等；
2、汽车：保险杆、分电盘、安全玻璃等；
3、工业零件：照相机本体、机具外壳、安全帽、潜水镜、安全镜片等；
4、光学照明：大型灯罩、防护玻璃、光学仪器的左右目镜筒等；
5、高精度零件：电子计算机、视频录象机等；
6、机械设备：各种齿轮、齿条、蜗轮、蜗杆、轴承、凸轮、螺栓、杠杆、曲轴、棘轮、机械设备壳体、罩盖及框架等；
7、医疗器材：医用杯、筒、瓶、牙科器械、药品容器和手术器械；
8、其它方面：建筑上用作中空筋双壁板、暖房玻璃等；纺织行业用作纺织纱管、纺织机轴瓦等；日用方面用作奶瓶、餐具、玩具、模型、绝缘接插件、线圈框架、管座、绝缘套管、矿灯的电池壳、绝缘皮包、录音带、彩色录象磁带等。
分类：防静电PC、导电PC、加纤防火PC、抗紫外线耐候PC、食品级PC。
产品使用时的注意事项
1.使用前必须将材料进行（烘料）干燥取理。
2.干燥及成型时，会挥发少量挥发性气体，对眼，鼻，喉咙会造成一定刺激。在进行这些热处理时，请进行适当的局部通风。
3.粒子如果洒落在地板上，为了避免滑倒，请立即进行清扫。
4.由于可能会发生散落的问题，需要进行产品堆积时请留意。
基础创新塑料PC DMX9455，阻燃PC