PA46 TS300荷兰---Supply PA46 / ts250f6 characteristic remarks: 30%glass reinforced, heat stable, flame retardant

Main properties: 30% glass fiber, heat stabilizer, heatstability, flame retardant. Important parameters: density: 1.68 g /cm3 molding shrinkage: 0.4% notch impact strength: 11 tensilestrength: 180 MPa bending modulus: 12000 MPa

Main properties: 40% glass fiber, heat stabilizer, heatstability, flame retardant. Important parameters: density: 1.77 g /cm3 molding shrinkage: 0.6% notch impact strength: 12 tensilestrength: 195 MPa bending modulus: 13000 MPa

Main properties: 30% glass fiber, flame retardant, flameretardant. Important parameters: density: 1.56 g / cm3 moldingshrinkage: 1.0% notched impact strength: 8 tensile strength: 170MPa bending modulus: 10000 MPa

Main properties: 40% glass fiber, flame retardant, flameretardant. Important parameters: density: 1.65 g / cm3 moldingshrinkage: 1.3% notched impact strength: 8 tensile strength: 180MPa bending modulus: 14000 MPa

Supply PA46 / TS300 NC important parameters: density: 1.41 g /cm3 water absorption: 2.6% molding shrinkage: 1.3% bending modulus:3900 MPa hot deformation temperature: 290 ℃

Supply PA46 / TS350 BK main performance: flame retardant, flameretardant. Important parameters: density: 1.41 g / cm3 waterabsorption: 2.6% molding shrinkage: 1.3% bending modulus: 3900 MPahot deformation temperature: 290 ℃

Main properties: 30% glass fiber, heat stabilizer, heatstability. Important parameters: density: 1.41 g / cm3 waterabsorption: 1.5% notched impact strength: 12 tensile strength: 210MPa elongation at break: 4%

PA46 / tw200fm33 BK main properties: 30% glass / mineral, lowwarpage. Important parameters: density: 1.42 g / cm3, notchedimpact strength: 16, tensile strength: 250 MPa, bending modulus:14000 MPa, hot deformation temperature: 290 ℃

Supply PA46 / tw241f6 characteristics remarks: 30% glass fiberreinforced, heat stabilizer, lubricant, heat stable, lubrication.Important parameters: density: 1.41 g / cm3 molding shrinkage: 1.2%notch impact strength: 4 bending modulus: 4700 MPa hot deformationtemperature: 290 ℃

PA46 / tw241f8 BK main properties: 40% glass fiber, heatstabilizer, lubricant, lubrication, thermal stability. Importantparameters: density: 1.51 g / cm3 molding shrinkage: 1.1% notchimpact strength: 14 bending modulus: 11500 MPa hot deformationtemperature: 290 ℃

Main properties: 50% glass fiber, heat stabilizer, heatstability. Important parameters: density: 1.62 g / cm3, notchedimpact strength: 16, tensile strength: 250 MPa, tensile modulus:7800 MPa, hot deformation temperature: 290 ℃

Supply PA46 / tw241f12 main performance: 60% glass fiber, heatstabilizer, good fluidity, thermal stability. Important parameters:density: 1.27 g / cm3, water absorption: 2.9%, molding shrinkage:1.5%, bending modulus: 3100 MPa, hot deformation temperature: 200℃

Main properties: 50% glass fiber, heat stabilizer, heatstability. Important parameters: density: 1.63 g / cm3, waterabsorption: 1.8%, molding shrinkage: 1.3%, bending modulus: 11000MPa, hot deformation temperature: 285 ℃

Main properties: 30% glass fiber, heat stabilizer, heatstability. Important parameters: density: 1.54 g / cm3 moldingshrinkage: 0.5% tensile strength: 190 MPa elongation at break: 3%hot deformation temperature: 290 ℃

Main properties: heat stabilizer, heat stability. Importantparameters: density: 1.18 g / cm3, molding shrinkage: 2.0%, hotdeformation temperature: 190 ℃