| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0070 in/in @Thickness 0.126 in | ASTM D955 |
| Melt Flow | 28 g/10 min @Load 10.0 kg, Temperature 220 °C | 28 g/10 min @Load 22.0 lb, Temperature 428 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 39.2 MPa @Thickness 3.20 mm | 5690 psi @Thickness 0.126 in | 50 mm/min; ASTM D638 |
| Elongation at Break | >= 10 % @Thickness 3.20 mm | >= 10 % @Thickness 0.126 in | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.66 GPa @Thickness 3.20 mm | 240 ksi @Thickness 0.126 in | 1 mm/min; ASTM D638 |
| Flexural Yield Strength | 64.7 MPa @Thickness 3.20 mm | 9390 psi @Thickness 0.126 in | 15 mm/min; ASTM D790 |
LG ABS PT270
成型性能
无定形材料,流动性中等,吸湿大,必须充分干燥,表面要求光泽的塑件须长时间预热干燥80-90度,3小时；
宜取高料温,高模温,但料温过高易分解(分解温度为>270度).对精度较高的塑件,模温宜取50-60度,对高光泽.耐热塑件,模温宜取60-80度；
如需解决夹水纹，需提高材料的流动性，采取高料温、高模温，或者改变入水位等方法；
如成形耐热级或阻燃级材料，生产3-7天后模具表面会残存塑料分解物，导致模具表面发亮，需对模具及时进行清理，同时模具表面需增加排气位置；
冷却速度快，模具浇注系统应以粗，短为原则，宜设冷料穴，浇口宜取大，如：直接浇口，圆盘浇口或扇形浇口等，但应防止内应力增大，必要时可采用调整式浇口。模具宜加热，应选用耐磨钢；
料温对塑件质量影响较大，料温过低会造成缺料，表面无光泽，银丝紊乱料温过高易溢边，出现银丝暗条，塑件变色起泡；
用途
ABS树脂的应用领域是汽车、电子电器和建材。汽车领域的使用包括汽车仪表板、车身外板、内装饰板、方向盘、隔音板、门锁、保险杠、通风管等很多部件。在电器方面则广泛应用于电冰箱、电视机、洗衣机、空调器、计算机、复印机等电子电器中。建材方面，ABS管材、ABS卫生洁具、ABS装饰板广泛应用于建材工业。此外ABS还广泛的应用于包装、家具、体育和娱乐用品、机械和仪表工业中。