高流动性ABS 台湾奇美ABS PA-746H
| 规格级别： | 高流动级 | 外观颜色： | --- |
| 用途概述： | 性能相当于PA-747，可注射成型大面或薄肉成型品，如摩托车侧盖挡板。 | ||
| 备注说明： | 产品特性：高流动性、高冲击强度 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.03 | 23/23℃ |
| 熔体流动速率 | 200℃×5kg | ASTM D-1238 | 4.8 | g/10min | |
| 熔体流动速率 | 220℃×10kg | ASTM D-1238 | 52 | g/10min | |
| 燃烧性 | File No. E56070 UL&C-UL | --- | 1/16"HB | --- | |
| 机械性能 | 引张强度 | --- | ASTM D-638 | 350 | kg/cm2 |
| 引张强度 | --- | ASTM D-638 | 4960 | kg/cm2 | |
| 伸长率 | --- | ASTM D-638 | 30 | % | |
| 弯曲弹性率 | --- | ASTM D-790 | 2.0×104 | kg/cm2 | |
| 弯曲弹性率 | --- | ASTM D-638 | 2.8×105 | lb/in2 | |
| 弯曲强度 | --- | ASTM D-790 | 560 | kg/cm2 | |
| 弯曲强度 | --- | ASTM D-790 | 8000 | lb/in2 | |
| 洛氏硬度 | --- | ASTM D-785 | 105 | R | |
| IZOD冲击强度 | 1/8" | ASTM D-256 | 30 | kg/cm2 | |
| IZOD冲击强度 | 1/8" | ASTM D-256 | 5.6 | ft.lb/in | |
| IZOD冲击强度 | 1/4" | ASTM D-256 | 25 | kg.cm/cm | |
| IZOD冲击强度 | 1/4" | ASTM D-256 | 4.6 | ft.lb/in | |
| 热 性 能 | 维卡软化点 | --- | ASTM D-1525 | 104 | ℃ |
| 维卡软化点 | --- | ASTM D-1525 | 219 | �H | |
| 热变形温度 | --- | ASTM D-648 | 96(205) | ℃ | |
| 热变形温度 | --- | ASTM D-648 | 86(187) | �H | |
塑料的密度鉴别法
塑料的品种不同，其密度也不同，可利用测定密度的方法来鉴别塑料，但此时应将发泡制品分别出来，因为发泡沫塑料的密度不是材料的真正的密度。在实际工业上，也有利用塑料的密度不同来分选塑料的
密度/（g/cm3） | 材料 | 密度/（g/cm3） | 材料 |
| 0．80 | 硅橡腔（可用二氧化硅填充到1。25） | 1．19~1．35 | 增塑聚氯乙烯（大约含有40%增塑剂） |
| 0．83 | 聚甲基戊烯 | 1．20~1．22 | 聚碳酸酯（双酚A型） |
| 0．85~0．91 | 聚丙烯 | 1．20~1．26 | 交联聚氨酯 |
| 0．89~0．93 | 高压（低密度）聚乙烯 | 1．26~1．28 | 苯酚甲醛树脂（未填充） |
| 0．91~0．92 | 1-聚丁烯 | 1．26~1．31 | 聚乙烯醇 |
| 0．9~0．93 | 聚异丁烯 | 1．25~1．35 | 乙酸纤维素 |