PA66 A3EG10 PA66 A3EG10

BASF PA66 Ultramid A3EG10物性参数物性表

以下是BASF PA66 Ultramid A3EG10中英文物性表

BASF Ultramid® A3EG10PA66(尼龙66-聚酰胺)

The property table is providedby www.plas-cn.com, welcome to download, reprintplease indicate the source!

Physical Properties物理性质

Metric公制数据

English英制数据

Comments测试方法

Bulk Density密度 

0.500 - 0.800 g/cc

0.0181 - 0.0289 lb/in³

Density密度 

1.56 g/cc

0.0564 lb/in³

ISO 1183

Water Absorption吸水率 

3.7 - 4.3 %

Saturation; ISO 62

Moisture Absorption atEquilibrium吸湿平衡 

1.0 - 1.4 %

23°C; 50% RH; ISO 62

Viscosity Measurement粘度 

130

ISO 307

Linear Mold Shrinkage 线性收缩率

0.0045 cm/cm

0.0045 in/in

restricted

Linear Mold Shrinkage,Flow线性收缩率/流动 

0.0033 cm/cm

0.0033 in/in

ISO 2577

0.0045 cm/cm

0.0045 in/in

TM=300°C, TW=80°C

Linear Mold Shrinkage,Transverse线性收缩率/横向 

0.0082 cm/cm

0.0082 in/in

ISO 2577

Melt Flow熔体流动速率 

31.2 g/10min
@Load 5.00kg,
Temperature 275 °C

31.2 g/10min
@Load 11.0lb,
Temperature 527 °F

ISO 1133

Mechanical Properties力学性能

Tensile Strength,Yield屈服拉伸强度 

240 MPa

34800 psi

50 mm/min; ISO 527-1/-2

Elongation at Yield屈服伸长率 

2.5 %

50 mm/min; ISO 527-1/-2

Modulus of Elasticity弹性模量 

16.8 GPa

2440 ksi

ISO 527-1/-2

Flexural Strength弯曲强度 

360 MPa

52200 psi

at max force; ISO 178

Flexural Modulus弯曲弹性模量 

15.0 GPa

2180 ksi

ISO 178

Izod Impact,Notched悬臂梁缺口冲击强度 (ISO) 

13.0 kJ/m²
@Temperature23.0 °C

6.19 ft-lb/in²
@Temperature73.4 °F

ISO 180/A

Charpy ImpactUnnotched夏比缺口试样冲击 

9.00 J/cm²
@Temperature-30.0 °C

42.8 ft-lb/in²
@Temperature-22.0 °F

ISO 179/1eU

9.50 J/cm²
@Temperature23.0 °C

45.2 ft-lb/in²
@Temperature73.4 °F

Charpy ImPAct, Notched夏比缺口冲击 

1.30 J/cm²
@Temperature-30.0 °C

6.19 ft-lb/in²
@Temperature-22.0 °F

ISO 179/1eA

1.80 J/cm²
@Temperature23.0 °C

8.57 ft-lb/in²
@Temperature73.4 °F

Electrical Properties电性能

Volume ResiSTivity体积电阻率 

1.00e+13 ohm-cm

IEC 60093

Dielectric Constant 介电常数

3.8
@Frequency 1.00Hz

IEC 60250

Dissipation Factor 耗散因数

0.015
@Frequency 1.00e+6Hz

IEC 60250

Comparative TrackingIndex 跟踪指数

550 V

Test solution A; IEC 60112

Thermal Properties热性能

CTE, linear, Parallel toFlow线性热膨胀系数 

0.0500 - 0.200 µm/m-°C
@Temperature 23.0 - 80.0 °C

0.0278 - 0.111 µin/in-°F
@Temperature 73.4 - 176 °F

DIN 11359-1/-2

CTE, linear, Transverse toFlow线性热膨胀系数/横向 

0.500 - 0.600 µm/m-°C
@Temperature 23.0 - 80.0 °C

0.278 - 0.333 µin/in-°F
@Temperature 73.4 - 176 °F

DIN 11359-1/-2

Specific Heat Capacity比热容 

1.30 J/g-°C

0.311 BTU/lb-°F

Thermal Conductivity导热系数 

0.370 W/m-K

2.57 BTU-in/hr-ft²-°F

DIN 52612

Melting Point熔点 

260 °C

500 °F

DIN 53765

Maximum Service Temperature,Air使用温度 

240 °C

464 °F

Deflection Temperatureat热变形温度0.46 MPa (66 psi) 

250 °C

482 °F

ISO 75-1/-2

Deflection Temperatureat热变形温度1.8 MPa (264 psi) 

250 °C

482 °F

ISO 75-1/-2

DecompositionTemperature分解温度 

>= 310 °C

>= 590 °F

Flammability, UL94阻燃等级 

HB
@Thickness 1.60mm

HB
@Thickness 0.0630in

Processing Properties加工性能

Processing Temperature加工温度 

80.0 °C

176 °F

Hopper Throat

Zone 1  1区

300 °C

572 °F

Feed zone

Zone 2  2区

300 °C

572 °F

Compression

Zone 3  3区

Metering-zone

Zone 4  4区

Nozzle

Melt Temperature熔体温度 

290 - 310 °C

554 - 590 °F

Injection-molding/Extrusion

300 °C

Optimal

Mold Temperature模具温度 

Optimal

80.0 - 90.0 °C

176 - 194 °F

Injection-molding

Drying Temperature干燥温度 

80.0 °C

176 °F

Dry Time干燥温度 

4 hour

Moisture Content水分含量 

0.030 - 0.060 %

<= 0.15 %

<= 0.15 %