PC EXL9330 BK1A068，耐寒PC原料，PC耐寒黑色颗粒，沙伯基础 EXL9330 BK1A068
厂家(产地)沙伯基础(原GE)牌号EXL9330-BK1A068加工级别注塑级特性级别阻燃级用途级别通用级销售方式品牌经销类型标准料
Lexan PC EXL9330物性
-60℃延展性,紫外稳定.耐燃性V-0/5VA. 非卤化,不含溴.
Property
| TYPICALPROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 50 mm/min | 590 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 620 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 130 | % | ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 21400 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 900 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 21000 | kgf/cm2 | ASTM D 790 | |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min | 60 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | 125 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2100 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 85 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 | |
| Hardness, H358/30 | 90 | MPa | ISO 2039-1 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C | 81 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, notched, -30°C | 69 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, notched, -50°C | 59 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, notched, 23°C, 6.4mm | 65 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, double-gated, 23°C | 108 | cm-kgf/cm | SABIC Method | |
| Instrumented Impact Total Energy, 23°C | 539 | cm-kgf | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U | |
| Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m2 | ISO 180/1U | |
| Izod Impact, notched 80*10*3 +23°C | 70 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 55 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 63.5*12.7*3.2, 23°C | 80 | kJ/m2 | ISO 180/4A | |
| Izod Impact, notched 63.5*12.7*3.2, -30°C | 65 | kJ/m2 | ISO 180/4A | |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 75 | kJ/m2 | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m2 | ISO 179/1eA | |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 | 142 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 134 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 124 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 6.66E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 6.66E-05 | 1/°C | ASTM E 831 | |
| CTE, 23°C to 80°C, flow | 7.2E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 7.7E-05 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate B/50 | 140 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 142 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 135 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 124 | °C | ISO 75/Ae | |
| Relative Temp Index, Elec | 125 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 115 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 120 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.18 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.8 | % | SABIC Method | |
| Mold Shrinkage, xflow, 3.2 mm | 0.4 - 0.8 | % | SABIC Method | |
| Melt Flow Rate, 300°C/1.2 kgf | 10 | g/10 min | ASTM D 1238 | |
| Density | 1.19 | g/cm2 | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.35 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.15 | % | ISO 62 | |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 9 | cm210 min | ISO 1133 | |
| ELECTRICAL | Value | Unit | Standard | |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 50/60 Hz | 2.95 | - | ASTM D 150 | |
| Relative Permittivity, 1 MHz | 2.9 | - | ASTM D 150 | |
| Dissipation Factor, 50/60 Hz | 0.0024 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.0085 | - | ASTM D 150 | |
| Hot Wire Ignition {PLC) | 1 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 50/60 Hz | 2.6 | - | IEC 60250 | |
| Relative Permittivity, 1 MHz | 2.7 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.008 | - | IEC 60250 | |
| Comparative Tracking Index | 225 | V | IEC 60112 | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94V-0 Flame Class Rating (3) | 1.49 | mm | UL 94 | |
| UL Recognized, 94-5VA Rating (3) | 2.99 | mm | UL 94 | |
| Glow Wire Flammability Index 960°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 825 | °C | IEC 60695-2-13 | |
| Oxygen Index (LOI) | 35 | % | ISO 4589 | |
| UV-light, water exposure/immersion | F1 | - | UL 746C | |
Processing
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time(Cumulative) | 48 | hrs |
| Maximum MoistureContent | 0.02 | % |
| Melt Temperature | 295 - 315 | °C |
| Nozzle Temperature | 290 - 310 | °C |
| Front - Zone 3Temperature | 295 - 315 | °C |
| Middle - Zone 2Temperature | 280 - 305 | °C |
| Rear - Zone 1Temperature | 215 - 295 | °C |
| Mold Temperature | 70 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to CylinderSize | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |