日本帝人PC L-1250Y 透明级pc
| 规格级别： | --- | 外观颜色： | --- |
| 用途概述： | 对流动性要求较高的薄壁制品、电器、电子元件、机械零件、劳保、医疗用品、照明器具及灯罩、餐具、容器。 | ||
| 备注说明： | 特性：Zui适宜于采用注坯吹塑成型 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24hr，in 23℃ | ASTM D-570 | 0.20 | % |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.20 | --- |
| 透光率 | 厚度3mm | ASTM D-1003 | 88 | % | |
| 折射率 | --- | ASTM D-542 | 1.585 | --- | |
| 阻燃性 | 厚度1.47mm | UL 94 | 94V-2 | --- | |
| 阻燃性 | 厚度3.05mm | UL 94 | 94V-2 | --- | |
| 机械性能 | 拉伸强度屈服点断裂点 | --- | ASTM D-638ASTM D-638 | 61(620)81(830) | Mpa(kgf/cm2)Mpa(kgf/cm2) |
| 拉伸模量 | --- | ASTM D-638 | 2120(21600) | Mpa(kgf/cm2) | |
| 拉伸率屈服点断裂点 | --- | ASTM D-638ASTM D-638 | 6140 | --- | |
| 弯曲强度 | --- | ASTM D-790 | 90(915) | Mpa(kgf/cm2) | |
| 弯曲模量 | --- | ASTM D-790 | 2230(22700) | Mpa(kgf/cm2) | |
| 压缩强度 | --- | ASTM D-695 | 76(770) | Mpa(kgf/cm2) | |
| 耐冲击强度值 | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 880(90) | j/m(kgf.cm/cm) | |
| 耐冲击强度值 | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 140(14) | j/m(kgf.cm/cm) | |
| 洛氏硬度 | --- | ASTM D-785 | 77 | M标度 | |
| 电气性能 | 耐导电径迹性（CTI） | --- | IEC 112 | 300 | V |
| 绝缘破坏强度 | 快速加压值厚度1.6mm | ASTM D-149 | 30 | KV/mm | |
| 体积电阻率 | --- | ASTM D-257 | 3 | 1016Ω.cm | |
| 介电率 | 60Hz | ASTM D-150 | 2.95 | --- | |
| 介电率 | 106Hz | ASTM D-150 | 2.9 | --- | |
| 介电正切 | 60Hz | ASTM D-150 | 0.0004 | --- | |
| 介电正切 | 106Hz | ASTM D-150 | 0.009 | --- | |
| 耐电弧性 | --- | ASTM D-495 | 110 | secc | |
| 加工性能 | 成型收缩率流动方向垂直方向 | --- | ASTM D-955ASTM D-955 | 0.5～0.70.5～0.7 | %% |
| 热 性 能 | 负荷挠曲温度 | 负荷0.451MPa(4.6kgf/cm) | ASTM D-648 | 143 | °C |
| 负荷挠曲温度 | 负荷1.813MPa(18.6kgf/cm) | ASTM D-648 | 143 | °C | |
| 线膨胀系数流动方向垂直方向 | --- | ASTM D-696ASTM D-696 | 77 | 10-5cm/cm/℃10-5cm/cm/℃ | |
| 温度指数电学式冲击式非冲击式 | 厚度1.47mm厚度1.47mm厚度1.47mm | UL 746BUL 746BUL 746B | 125115125 | °C°C°C | |