420SE0 Resin 物性表
物理性能额定值单位测试方法比重1.63g/cm³ASTM D792, ISO 1183熔流率 (250°C/5.0 kg)42g/10minASTM D1238溶化体积流率 (MVR250°C/5.0 kg)29.0cm³/10minISO 1133收缩率(流动)0.10 到 0.50%Internal Method(流动: 3.20 mm)0.50 到 0.70%InternalMethod (横向流动)0.40 到0.80%InternalMethod (横向流动: 3.20 mm)0.50 到 1.0%InternalMethod吸水率 (饱和, 23°C)0.090%ISO 62(平衡, 23°C, 50% RH)0.070%ISO62特定体积0.610cm³/gASTM D792洛氏硬度 ((R 计秤))119
ASTM D785, ASTM D785球压硬度 ((H 358/30))118MPaISO2039-1机械性能额定值单位测试方法拉伸模量12000MPaASTM D638
10000MPaISO 527-2/1抗张强度 (屈服)120MPaASTM D638
(屈服)120MPaISO527-2/5 (断裂)120MPaASTMD638 (断裂)120MPaISO 527-2/5伸长率 (屈服)2.0%ASTMD638
(屈服)1.9%ISO527-2/5 (断裂)2.0%ASTMD638 (断裂)1.9%ISO 527-2/5弯曲模量 (50.0mm 跨距)9800MPaASTM D790
9500MPaISO 178
180MPaISO 178 (断裂, 50.0mm 跨距)186MPaASTM D790抗泰伯磨耗 (1000 Cycles,1000 g, CS-17转轮)22.0mgInternal Method简支梁缺口冲击强度 (-30°C)6.0kJ/m²ISO179/1eA(23°C)7.0kJ/m²ISO 179/1eA简支梁缺口冲击强度 (-30°C)50kJ/m²ISO179/1eU(23°C)50kJ/m²ISO 179/1eU悬壁梁缺口冲击强度 (-30°C)57.0J/mASTMD256
(23°C)60.0J/mASTMD256 (-30°C)6.00kJ/m²ISO180/1A (23°C)7.00kJ/m²ISO 180/1A无缺口悬臂梁冲击(23°C)620J/mASTM D4812
(-30°C)45.0kJ/m²ISO180/1U (23°C)45.0kJ/m²ISO 180/1U装有测量仪表的落镖冲击(23°C, Total Energy)5.00JASTM D3763热性能额定值单位测试方法热变形温度 (0.45 MPa,未退火, 3.20 mm)212°CASTM D648
(0.45 MPa, 未退火, 100mm 跨距)220°CISO 75-2/Be (1.8 MPa, 未退火,3.20 mm)200°CASTM D648 (1.8 MPa,未退火, 100 mm 跨距)195°CISO75-2/Ae (1.8 MPa, 未退火, 64.0mm 跨距)200°CISO 75-2/Af维卡软化温度200°CASTM D1525
200°CISO 306/B50
200°CISO 306/B120
220°CISO 306/A50 (BallPressureTest125°C)Pass
IEC 60695-10-2线形膨胀系数 (流动: -40 到 40°C)0.000025cm/cm/°CASTM E831, ISO11359-2
(流动: 23 到 80°C)0.000025cm/cm/°CISO11359-2 (横向: -40 到 40°C)0.000089cm/cm/°CASTME831, ISO 11359-2 (横向: 23 到80°C)0.00012cm/cm/°CISO 11359-2导热系数0.25
ISO 8302电气性能额定值单位测试方法体积电阻率> 1.0E+15ohmsIEC 60093
> 1.0E+15ohm·cmASTM D257, IEC 60093介电强度 (1.60 mm, inOil)24kV/mmASTM D149
(3.20 mm, in Air)19kV/mmASTMD149 (0.800 mm, 在油中)23kV/mmIEC60243-1 (1.60 mm, 在油中)22kV/mmIEC60243-1 (3.20 mm, 在油中)16kV/mmIEC 60243-1介电常数(100 Hz)3.80
ASTM D150, IEC 60250
(1 MHz)3.70
ASTM D150 (50 Hz)3.30
IEC 60250 (60 Hz)3.30
IEC 60250 (1 MHz)3.30
IEC 60250耗散因数 (100 Hz)0.0020
ASTM D150, IEC 60250
(1 MHz)0.020
ASTM D150 (50 Hz)0.0010
IEC 60250 (60 Hz)0.0010
IEC 60250 (1 MHz)0.010
IEC 60250耐电弧性 (PLC)PLC 6
ASTM D495漏电起痕指数175VIEC 60112(解决方案 B)125VIEC 60112