PPA美国苏威AS-4133L增强玻纤33%经润滑PPA高温塑料
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.45 | g/cm3 | |
| 成型收缩率 | 流动 | ASTM D955 | 0.5 | % | |
| 横向 | ASTM D955 | 1.0 | % | ||
| 吸水率 | 23H | ASTM D570 | 0.29 | % | |
| 机械性能 | 拉伸模量 | ASTM D638 | 11700 | MPa | |
| 拉伸应力 | ASTM D527-2 | 172 | MPa | ||
| 拉伸伸长率 | break | ASTM D638 | 2.2 | % | |
| 弯曲模量 | ASTM D790 | 11000 | MPa | ||
| 弯曲强度 | ASTM D790 | 241 | MPa | ||
| Charpy缺口冲击强度 | 23℃ | ASTM D256 | 80.1 | J/m | |
| Charpy无缺口冲击强度 | -30℃ | ASTM D256 | 961 | J/m | |
| 热性能 | 热变形温度 | 0.45MPa,退火，3.18mm | ASTM D648 | 320 | ℃ |
| 1.8MPa,退火，3.18mm | ASTM D648 | 300 | ℃ | ||
| 线性膨胀系数 | 流动 | ASTM D696 | 0.000022 | cm/cm/℃ | |
| 横向 | ASTM D696 | 0.000059 | cm/cm/℃ | ||
| 电气性能 | 体积电阻率 | ASTM D257 | 2.0E+16 | ohm*cm | |
| 电气强度 | ASTM D149 | 20 | KV/mm | ||
| 介电常数 | 60HZ | ASTM D150 | 4.30 | ||
| 1MHZ | ASTM D150 | 3.40 | |||
| 介质损耗因数 | 60HZ | ASTM D150 | 0.020 | ||
| 1MHZ | ASTM D150 | 0.019 | |||
| 耐导电径迹性 | UL 746 | 600 | V | ||
| 其它 | 阻燃等级 | UL 94 | HB | ||