PA66 22C NC010 矿物/玻纤38%增强,热稳定

DuPont™ Minlon® 数据
杜邦™minlon® 数据
mineral reinforced nylon resin
矿物增强尼龙树脂

Minlon ® 22C NC010 is a 38% mineral/glass reinforced, heatstabilized polyamide 66 resin for injection molding.
minlon®22C NC010 是38%矿物/玻璃纤维增强，热稳定聚酰胺66树脂注塑成型。

Property

Test Method

Value

Units

DAM           50%RH

Identification

Resin Identification

Part Marking Code

ISO 1043

ISO 11469

PA66-(MD+GF)38

>PA66-(MD+GF)38<

Mechanical

Stress at Break

Strain at Break

Tensile Modulus

Flexural Modulus

Notched Charpy Impact Strength

-40°C (-40°F)

-30°C (-22°F)

23°C (73°F)

Unnotched Charpy Impact Strength

ISO 527

ISO 178

ISO 179/1eA

ISO 179/1eU

MPa (kpsi)

%

2

kJ/m

130 (18.9)

3.5

7500 (1090)

6500 (940)

3

4

40

50

82 (11.9)

10

5000 (725)

6

35

45

DAM

50%RH

Thermal

Deflection Temperature

0.45MPa

1.80MPa

Melting Temperature

10°C/min

CLTE, Normal

-40 - 23°C (-40 - 73°F)

23 - 55°C (73 - 130°F)

55 - 160°C (130 - 320°F)

CLTE, Parallel

ISO 75f

ISO 11357-1/-3

ISO 11359-1/-2

°C (°F)

E-4/C (E-4/F)

255 (491)

230 (446)

263 (505)

0.53 (0.29)

0.62 (0.33)

1.0 (0.56)

0.39 (0.22)

0.41 (0.23)

0.36 (0.20)

Electrical

Relative Permittivity

1E2 Hz

1E6 Hz

Volume Resistivity

Dissipation Factor

Electric Strength

2.0mm

CTI

3.0mm

IEC 60250

IEC 60093

IEC 60243-1

UL 746A

ohm m

E-4

kV/mm (V/mil)

V

1E11

100

20 (510)

475

7

1E7

200

500

18 (460)

Flammability

Flammability Classification

0.81mm

Oxygen Index

High Amperage Arc Ignition Resistance

1.5mm

Hot Wire Ignition

IEC 60695-11-10

UL94

ISO 4589-1/-2

arcs

s

HB

24

>200

117

120

Temperature Index

RTI, Electrical

RTI, Impact

RTI, Strength

UL 746B

°C

65

Other

Density

Water Absorption

Equilibrium 50%RH

Immersion 24h, 2.0mm

Saturation, immersed

Molding Shrinkage

Normal, 2.0mm

Parallel, 2.0mm

ISO 1183

ISO 62, Similar to

ISO 294-4

3      3

kg/m (g/cm )

1450 (1.45)

1.4

1.0

5.4

0.9

0.7

Mold Shrinkage

Flow, 1.6mm (0.062in)

Flow, 3.2mm (0.126in)

Flow, 6.4mm (0.25in)

Transverse, 1.6mm (0.062in)

Transverse, 3.2mm (0.126in)

Transverse, 6.4mm (0.25in)

0.6

0.8

1.1

Processing

Melt Temperature Range

Melt Temperature Optimum

Mold Temperature Range

Mold Temperature Optimum

Drying Time, Dehumidified Dryer

Drying Temperature

Processing Moisture Content

h

285-305 (545-580)

295 (560)

70-120 (160-250)

100 (210)

2-4

80 (175)

<0.20