PA66 ST801，PA66 ST801 美国杜邦 增韧，耐寒
DuPont Zytel® ST801 Nylon66（聚酰胺-尼龙66）
The property table is providedby www.cn-plas.com, welcome to download, reprintplease indicate the source!
Physical Properties物理性质
Metric公制数据
English英制数据
Comments测试方法
Density密度
1.11 g/cc
0.0401 lb/in³
DAM; ISO 1183
Water Absorption吸水率
1.28 %
@Temperature 23.0 °C
1.28 %
@Temperature 73.4 °F
Immersion 24h; DAM; ISO 62, Similar to
1.3 %
@Temperature 23.0 °C
1.3 %
@Temperature 73.4 °F
Immersion 24h; DAM; ASTM D570
4.9 %
@Thickness 1.00 mm,
Temperature 23.0 °C
4.9 %
@Thickness 0.0394 in,
Temperature 73.4 °F
Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage,Flow线性收缩率/流动
0.015 cm/cm
@Thickness 2.00 mm
0.015 in/in
@Thickness 0.0787 in
Parallel; DAM; ISO 294-4
Linear Mold Shrinkage,Transverse线性收缩率/横向
0.017 cm/cm
@Thickness 2.00 mm
0.017 in/in
@Thickness 0.0787 in
Normal; DAM; ISO 294-4
Mechanical Properties力学性能
Tensile Stress拉伸应力
25.0 MPa
@Strain 50.0 %,
Temperature 150 °C
3630 psi
@Strain 50.0 %,
Temperature 302 °F
50%RH; ISO 527
38.0 MPa
@Strain 50.0 %,
Temperature 100 °C
5510 psi
@Strain 50.0 %,
Temperature 212 °F
DAM; ISO 527
44.0 MPa
@Strain 50.0 %,
Temperature 23.0 °C
6380 psi
@Strain 50.0 %,
Temperature 73.4 °F
65.0 MPa
@Strain 50.0 %,
Temperature 23.0 °C
9430 psi
@Strain 50.0 %,
Temperature 73.4 °F
84.0 MPa
@Strain 50.0 %,
Temperature -40.0 °C
12200 psi
@Strain 50.0 %,
Temperature -40.0 °F
95.0 MPa
@Strain 50.0 %,
Temperature -40.0 °C
13800 psi
@Strain 50.0 %,
Temperature -40.0 °F
Tensile Strength, Yield屈服拉伸强度
25.0 MPa
@Temperature 120 °C
3630 psi
@Temperature 248 °F
50%RH; ISO 527
33.0 MPa
@Temperature 100 °C
4790 psi
@Temperature 212 °F
DAM; ISO 527
杜邦™ Zytel® PA66ST801共聚物的一个特种阻燃牌号已用于生产光伏系统的逆变器模块罩（取代以前的金属罩）。 根据 325 V 的 CTI 值（CTI =相对电痕指数）、960°C 的 GWFI 值（GWFI = 灼热丝可燃指数）以及根据 UL94 V-0 易燃性标准的分类，Zytel®罩可满足特性要求。 该材料在注塑成型期间不易翘曲和收缩，加上加强筋等结构改进，使其能够满足甚至Zui为严格的制造公差标准。这样可以在使用铸铝制造的其他外壳部分上实现高精度贴合。 此外，使用 Zytel®能够为可见的部件提供更好的表面质量。