代理科思创TPU 1196 耐磨管材级
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D-792, ISO 1183 | 1.12 | g/cm3; | |
| 收缩率 | 流动 2.54 mm | ASTM D-955 | 0.80 | % | |
| 横向流动 2.54 mm | ISO 294-4 | 0.80 | % | ||
| 流量 2.54 mm | ISO 294-4 | 0.80 | % | ||
| 硬度计硬度 | 支撐 A | ASTM D-2240, ISO 868 | 87 | ||
| 支撐 D | ASTM D2240, ISO 868 | 36 | |||
机械性能 | 弯曲模量 | -30℃ | ASTM D-790, ISO 178 | 93.1 | MPa |
| 23℃ | ASTM D-790, ISO 178 | 34.5 | MPa | ||
| 抗泰伯磨耗 | 1000 Cycles, 1000 g, H-18 转轮 | ASTM D-1044 | 25.0 | mg | |
| 拉伸应力 | 应变 | ASTM D-412, ISO 37 | 6.20 | MPa | |
| 300%应变 | ASTM D-412, ISO 37 | 11.0 | MPa | ||
| 抗张强度 | 屈服 | ASTM D-412, ISO 37 | 34.5 | MPa | |
| 伸长率 | 屈服 | ASTM D-412, ISO 37 | 500 | % | |
| 撕裂强度 | ASTM D624 | 87.6 | kN/m | ||
| ISO 34-1 | 88 | kN/m | |||
| 压缩变形 | 23℃, 22.0 hr | ASTM D-395, ISO 815 | 13 | % | |
| 70℃, 22.0 hr | ASTM D-395, ISO 815 | 37 | % | ||
| 巴肖氏弹性 | ASTM D-2632 | 32 | % | ||
| 玻璃转化温度 | DSC | -40.0 | ℃ | |
| 维卡软化温度 | ISO 306/A50, ASTM D1525 4 | 91.1 | ℃ | ||