TPE美国杜邦 5556
物理性能额定值 (公制)额定值 (英制)测试方法密度1.03 g/cc0.0372 lb/in³
1.19 g/cc0.0430 lb/in³ISO 1183吸水率0.60 %
@Thickness 2.00 mm
0.60 %
@Thickness 0.0787 in
Sim. to ISO 62水分吸收0.200 %
0.200 %
Sim. to ISO 62饱和吸水率0.60 %0.60 %Immersion 24h; ASTM D570粘度81295cP
@Shear Rate 5000 1/s, Temperature 240 °C
81295 cP
@Shear Rate 5000 1/s, Temperature 464 °F
ISO 11403-1 -2
88320 cP
@Shear Rate 5000 1/s, Temperature 230 °C
88320 cP
@Shear Rate 5000 1/s, Temperature 446 °F
ISO 11403-1 -2
96440 cP
@Shear Rate 5000 1/s, Temperature 220 °C
96440 cP
@Shear Rate 5000 1/s, Temperature 428 °F
ISO 11403-1 -2
321800 cP
@Shear Rate 500 1/s, Temperature 240 °C
321800 cP
@Shear Rate 500 1/s, Temperature 464 °F
ISO 11403-1 -2
358400 cP
@Shear Rate 500 1/s, Temperature 230 °C
358400 cP
@Shear Rate 500 1/s, Temperature 446 °F
ISO 11403-1 -2
400200 cP
@Shear Rate 500 1/s, Temperature 220 °C
400200 cP
@Shear Rate 500 1/s, Temperature 428 °F
ISO 11403-1 -2线性成型收缩率,Flow0.014 cm/cm0.014 in/inISO 294-42577线性成型收缩率，横向0.014 cm/cm0.014 in/inISO 294-4 2577熔体流动速率7.0 g/10min
@Load 2.16 kg, Temperature 220 °C
7.0 g/10 min
@Load 4.76 lb, Temperature 428 °F
cm³/10min; ISO 1133
7.8 g/10 min
7.8 g/10 min
ISO 1133机械性能额定值 (公制)额定值 (英制)测试方法肖氏硬度 (邵氏 D)515115s; ISO 868
<= 55<= 55ISO 868抗张强度(断裂)40.0 MPa5800 psiISO 527-1/-2抗张强度6.90MPa
@Strain 5.00 %
1000 psi
ISO 527-1/-2
11.0 MPa
@Strain 10.0 %
1600 psi
ISO 527-1/-2
14.5 MPa
@Strain 50.0 %
2100 psi
ISO 527-1/-2
16.0 MPa
@Strain 100 %
2320 psi
ISO 527-1/-2
3.97 MPa
@Strain 6.94 %, Temperature 120 °C
576 psi
@Strain 6.94 %, Temperature 248 °F
TPE; ISO 11403-1 -2
4.65 MPa
@Strain 6.90 %, Temperature 100 °C
674 psi
@Strain 6.90 %, Temperature 212 °F
TPE; ISO 11403-1 -2
4.93 MPa
@Strain 6.00 %, Temperature 90.0 °C
715 psi
@Strain 6.00 %, Temperature 194 °F
ISO 11403-1 -2
4.97 MPa
@Strain 6.87 %, Temperature 90.0 °C
721 psi
@Strain 6.87 %, Temperature 194 °F
TPE; ISO 11403-1 -2
5.78 MPa
@Strain 16.44 %, Temperature 120 °C
838 psi
@Strain 16.44 %, Temperature 248 °F
TPE; ISO 11403-1 -2
6.37 MPa
@Strain 26.67 %, Temperature 120 °C
924 psi
@Strain 26.67 %, Temperature 248 °F
TPE; ISO 11403-1 -2
6.55 MPa
@Strain 36.16 %, Temperature 120 °C
950 psi
@Strain 36.16 %, Temperature 248 °F
TPE; ISO 11403-1 -2
6.62 MPa
@Strain 46.39 %, Temperature 120 °C
960 psi
@Strain 46.39 %, Temperature 248 °F
TPE; ISO 11403-1 -2
6.70 MPa
@Strain 58.81 %, Temperature 120 °C
972 psi
@Strain 58.81 %, Temperature 248 °F
TPE; ISO 11403-1 -2
6.83 MPa
@Strain 71.96 %, Temperature 120 °C
991 psi
@Strain 71.96 %, Temperature 248 °F
TPE; ISO 11403-1 -2
6.84 MPa
@Strain 7.55 %, Temperature 60.0 °C
992 psi
@Strain 7.55 %, Temperature 140 °F
TPE; ISO 11403-1 -2
6.97 MPa
@Strain 85.11 %, Temperature 120 °C
1010 psi
@Strain 85.11 %, Temperature 248 °F
TPE; ISO 11403-1 -2
6.98 MPa
@Strain 17.06 %, Temperature 100 °C
@Strain 17.06 %, Temperature 212 °F
TPE; ISO 11403-1 -2
7.12 MPa
@Strain 98.26 %, Temperature 120 °C
1030 psi
@Strain 98.26 %, Temperature 248 °F
TPE; ISO 11403-1 -2
7.41 MPa
@Strain 117.99 %, Temperature 120 °C
1070 psi
@Strain 117.99 %, Temperature 248 °F
TPE; ISO 11403-1 -2
7.46 MPa
@Strain 6.00 %, Temperature 40.0 °C
1080 psi
@Strain 6.00 %, Temperature 104 °F
ISO 11403-1 -2
7.51 MPa
@Strain 16.99 %, Temperature 90.0 °C
1090 psi
@Strain 16.99 %, Temperature 194 °F
TPE; ISO 11403-1 -2
7.67 MPa
@Strain 27.23 %, Temperature 100 °C
1110 psi
@Strain 27.23 %, Temperature 212 °F
@Strain 131.14 %, Temperature 120 °C
@Strain 131.14 %, Temperature 248 °F
TPE; ISO 11403-1 -2
7.88 MPa
@Strain 37.39 %, Temperature 100 °C
1140 psi
@Strain 37.39 %, Temperature 212 °F
TPE; ISO 11403-1 -2
7.90 MPa
@Strain 6.00 %, Temperature 23.0 °C
1150 psi
@Strain 6.00 %, Temperature 73.4 °F
ISO 11403-1 -2
7.96 MPa
@Strain 46.83 %, Temperature 100 °C
@Strain 46.83 %, Temperature 212 °F
TPE; ISO 11403-1 -2
8.04 MPa
@Strain 60.62 %, Temperature 100 °C
1170 psi
@Strain 60.62 %, Temperature 212 °F
TPE; ISO 11403-1 -2
8.07 MPa
@Strain 147.21 %, Temperature 120 °C
@Strain 147.21 %, Temperature 248 °F
TPE; ISO 11403-1 -2
8.17 MPa
@Strain 73.69 %, Temperature 100 °C
1180 psi
@Strain 73.69 %, Temperature 212 °F
TPE; ISO 11403-1 -2
8.30 MPa
@Strain 27.11 %, Temperature 90.0 °C
1200 psi
@Strain 27.11 %, Temperature 194 °F
TPE; ISO 11403-1 -2
8.32 MPa
@Strain 86.76 %, Temperature 100 °C
1210 psi
@Strain 86.76 %, Temperature 212 °F
TPE; ISO 11403-1 -2
8.52 MPa
@Strain 100.56 %, Temperature 100 °C
1240 psi
@Strain 100.56 %, Temperature 212 °F
@Strain 24.0 %, Temperature 90.0 °C
@Strain 24.0 %, Temperature 194 °F
ISO 11403-1 -2
8.56 MPa
@Strain 37.24 %, Temperature 90.0 °C
@Strain 37.24 %, Temperature 194 °F
TPE; ISO 11403-1 -2
8.65 MPa
@Strain 47.36 %, Temperature 90.0 °C
1250 psi
@Strain 47.36 %, Temperature 194 °F
TPE; ISO 11403-1 -2
8.67 MPa
@Strain 7.52 %, Temperature 40.0 °C
1260 psi
@Strain 7.52 %, Temperature 104 °F
TPE; ISO 11403-1 -2
8.76 MPa
@Strain 170.59 %, Temperature 120 °C
1270 psi
@Strain 170.59 %, Temperature 248 °F
TPE; ISO 11403-1 -2
8.78 MPa
@Strain 60.37 %, Temperature 90.0 °C
@Strain 60.37 %, Temperature 194 °F
TPE; ISO 11403-1 -2
8.85 MPa
@Strain 120.16 %, Temperature 100 °C
1280 psi
@Strain 120.16 %, Temperature 212 °F
TPE; ISO 11403-1 -2
8.94 MPa
@Strain 73.39 %, Temperature 90.0 °C
1300 psi
@Strain 73.39 %, Temperature 194 °F
TPE; ISO 11403-1 -2
9.14 MPa
@Strain 87.12 %, Temperature 90.0 °C
1330 psi
@Strain 87.12 %, Temperature 194 °F
TPE; ISO 11403-1 -2
9.17 MPa
@Strain 133.96 %, Temperature 100 °C
@Strain 133.96 %, Temperature 212 °F
TPE; ISO 11403-1 -2
9.33 MPa
@Strain 100.14 %, Temperature 90.0 °C
1350 psi
@Strain 100.14 %, Temperature 194 °F
TPE; ISO 11403-1 -2
9.60 MPa
@Strain 196.16 %, Temperature 120 °C
1390 psi
@Strain 196.16 %, Temperature 248 °F
TPE; ISO 11403-1 -2
9.61 MPa
@Strain 150.65 %, Temperature 100 °C
@Strain 150.65 %, Temperature 212 °F
TPE; ISO 11403-1 -2
9.71 MPa
@Strain 120.38 %, Temperature 90.0 °C
1410 psi
@Strain 120.38 %, Temperature 194 °F
TPE; ISO 11403-1 -2
9.82 MPa
@Strain 17.63 %, Temperature 60.0 °C
1420 psi
@Strain 17.63 %, Temperature 140 °F
TPE; ISO 11403-1 -2
10.01 MPa
@Strain 133.4 %, Temperature 90.0 °C
1452 psi
@Strain 133.4 %, Temperature 194 °F
TPE; ISO 11403-1 -2
TPE是热塑性聚氨酯弹性体橡胶。主要分为硬度范围宽（0-85D）、耐磨、耐油，透明，弹性好，在日用品、体育用品、玩具、装饰材料等领域得到广泛应用，无卤阻燃TPE还可以代替软质PVC以满足越来越多领域的环保要求，TPE出现在2015年，TPE薄膜消费量约占TPE产品总消费量的20%，TPE薄膜平均销售价格约4万元/吨，按照2013年我国TPE产品消费量23万吨计算，TPE薄膜消费量约为4.6万吨，市场消费额约18.4亿元，预计，2013-2017年TPE市场规模年均增长速度为11.2%，2017年达到28.1亿元，TPE现在是越来越受到大家欢迎。