DuPont Zytel® nylon resin
杜邦Zytel® 尼龙树脂
Glass Reinforced Resins
玻璃纤维增强树脂
Zytel® 70G33L NC010 is a 33% glass fiber reinforced polyamide 66resin for injection molding.
zytel®70G33L NC010是一个33%玻璃纤维增强聚酰胺66树脂注塑。
Property
Test Method
Units
Value
DAM
50%RH
Identification
Resin Identification
Part Marking Code
ISO 1043
ISO 11469
PA66-GF33
>PA66-GF33<
Mechanical
Stress at Break
Strain at Break
Tensile Modulus
Poisson's Ratio
Flexural Modulus
Flexural Strength
Notched Charpy Impact Strength
-40℃(-40℉)
-30℃(-22℉)
23℃(73℉)
Unnotched Charpy Impact Strength
ISO 527
ISO 527
ISO 178
ISO 179/1eA
ISO 179/1eU
MPa(kpsi)
%
MPa(kpsi)
2
kJ/m
200(29.0)
3.5
10500(1520)
0.39
9300(1350)
290(42)
10
13
70
85
140(20.3)
5
8000(1160)
6205(900)
200(29)
17
75
100
Thermal
Deflection Temperature
0.45MPa
1.80MPa
Melting Temperature
10℃/min
CLTE, Normal
-40-23℃(-40-73℉)
23-55℃(73-130℉)
55-160℃(130-320℉)
CLTE, Parallel
ISO 75f
ISO 11357-1/-3
ISO 11359-1/-2
℃(℉)
℃(℉)
E-4/C(E-4/F)
261(502)
252(486)
262(504)
0.65(0.36)
0.83(0.46)
1.37(0.76)
0.24(0.13)
0.18(0.10)
0.13(0.07)
Electrical
Relative Permittivity
1E2 Hz
1E6 Hz
Volume Resistivity
Dissipation Factor
CTI
3.0mm
IEC 60250
IEC 60093
IEC 60250
UL 746A
ohm m
E-4
V
4.2
4.0
1E13
150
600
Flammability
Flammability Classification
0.71mm
Oxygen Index
High Amperage Arc Ignition Resistance
0.75mm
High Voltage Arc Tracking Rate
Hot Wire Ignition
1.5mm
UL94
ISO 4589-1/-2
%
arcs
mm/min(in/min)
s
HB
24
>200
32.2(1.27)
8
6
9
Temperature Index
RTI, Electrical
RTI, Impact
RTI, Strength
UL 746B
UL 746B
℃
℃
130
120
130
Other
Density
Water Absorption
Equilibrium 50%RH
Immersion 24h, 2.0mm
Saturation, immersed
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
ISO 1183
ISO 62, Similar to
ISO 294-4
3 3
kg/m(g/cm )
1390(1.39)
1.8
1.2
5.7
1.1
0.3
Other
Mold Shrinkage
Flow, 1.6mm(0.063in)
Flow, 3.2mm(0.126in)
Flow, 6.4mm(0.25in)
Transverse, 1.6mm(0.063in)
Transverse, 3.2mm(0.126in)
Transverse, 6.4mm(0.25in)
%
0.2
0.5
1.0
Processing
Melt Temperature Range
Melt Temperature Optimum
Mold Temperature Range
Mold Temperature Optimum
Drying Time, Dehumidified Dryer
Drying Temperature
Processing Moisture Content
℃(℉)
h
285-305(545-580)
295(565)
70-120(160-250)
100(210)
2-4
80(175)
<0.20
Contact DuPont for Material Safety Data Sheet, general guidesand/or additional information about ventilation, handling, purging,drying, etc. ISO Mechanical properties measured at 4.0mm, ISOElectrical properties measured at 2.0mm, and all ASTM propertiesmeasured at 3.2mm.
Test temperatures are 23℃ unless otherwisestated.
The DuPont Oval Logo, DuPont™, The miracles of science™ andZytel® are trademarks or registered trademarks of DuPont Company.Copyright© 2005.