PA66美国杜邦10B140 BK061代理商

DuPont Performance Polymers Minlon® 10B140 BK061 Nylon 66(Unverified Data**) 物性表

物理性能额定值 (公制)额定值 (英制)测试方法密度1.50 g/cc0.0542 lb/in³DAM; ISO 1183填料含量40%40 %DAMWater Absorption1.6 %

@Temperature 23.0 °C

1.6 %

@Temperature 73.4 °F

Equilibrium 50%RH; DAM; ISO 62, Similar to
5.0 %

@Temperature 23.0 °C

5.0 %

@Temperature 73.4 °F

Saturation, immersed; DAM; ISO 62, Similar to机械性能额定值 (公制)额定值(英制)测试方法抗张强度(断裂)54.0 MPa

@Temperature 23.0 °C

7830 psi

@Temperature 73.4 °F

50%RH; ISO 527
82.0 MPa

@Temperature 23.0 °C

11900 psi

@Temperature 73.4 °F

DAM; ISO 527伸长率 (断裂)3.5 %

@Temperature 23.0 °C

3.5 %

@Temperature 73.4 °F

DAM; ISO 527
9.0 %

@Temperature 23.0 °C

9.0 %

@Temperature 73.4 °F

50%RH; ISO 527拉伸模量3.80 GPa

@Temperature 23.0 °C

551 ksi

@Temperature 73.4 °F

50%RH; ISO 527
6.60 GPa

@Temperature 23.0 °C

957 ksi

@Temperature 73.4 °F

DAM; ISO 527悬壁梁缺口冲击强度3.50 kJ/m²

@Temperature 23.0 °C

1.67 ft-lb/in²

@Temperature 73.4 °F

DAM; ISO 180/1A
4.00 kJ/m²

@Temperature 23.0 °C

1.90 ft-lb/in²

@Temperature 73.4 °F

50%RH; ISO 180/1A简支梁无缺口冲击强度3.50 J/cm²

@Temperature 23.0 °C

16.7 ft-lb/in²

@Temperature 73.4 °F

DAM; ISO 179/1eU
6.00 J/cm²

@Temperature 23.0 °C

28.6 ft-lb/in²

@Temperature 73.4 °F

50%RH; ISO 179/1eU简支梁缺口冲击强度0.350 J/cm²

@Temperature 23.0 °C

DAM; ISO 179/1eA
0.450 J/cm²

@Temperature 23.0 °C

2.14 ft-lb/in²

@Temperature 73.4 °F

50%RH; ISO 179/1eA电气性能额定值 (公制)额定值 (英制)测试方法相比耐漏电起痕指数(CTI)>= 600 V

@Temperature 23.0 °C

>= 600 V

@Temperature 73.4 °F

DAM; UL 746A热性能额定值 (公制)额定值 (英制)测试方法熔融温度263 °C505 °F10°C/min; DAM;ISO 11357-1/-3载荷下热变形温度(0.46 MPa)240 °C464 °FDAM; ISO75-1/-2载荷下热变形温度(1.8 MPa)170 °C338 °FDAM; ISO 75-1/-2UL RTI105 °C

@Thickness 0.710 mm

221 °F

@Thickness 0.0280 in

DAM; UL 746B
120 °C

@Thickness 3.00 mm

248 °F

@Thickness 0.118 in

DAM; UL 746B
120 °C

@Thickness 1.50 mm

248 °F

@Thickness 0.0591 in

DAM; UL 746BUL RTI，机械冲击65.0 °C

@Thickness 0.710 mm

149 °F

@Thickness 0.0280 in

DAM; UL 746B
105 °C

@Thickness 1.50 mm

221 °F

@Thickness 0.0591 in

DAM; UL 746B
115 °C

@Thickness 3.00 mm

239 °F

@Thickness 0.118 in

DAM; UL 746BUL RTI，机械无冲击65.0 °C

@Thickness 0.710 mm

DAM; UL 746B
115 °C

@Thickness 1.50 mm

239 °F

@Thickness 0.0591 in

DAM; UL 746B可燃性(UL94)HB

@Thickness 1.50 mm

HB

@Thickness 0.0591 in

DAM; UL94
HB

@Thickness 0.710 mm

HB

@Thickness 0.0280 in

DAM; UL94
HB

@Thickness 3.00 mm

HB

@Thickness 0.118 in

DAM; IEC 60695-11-10
HB

@Thickness 1.50 mm

DAM; IEC 60695-11-10
HB

@Thickness 0.710 mm

DAM; IEC 60695-11-10加工性能额定值 (公制)额定值 (英制)测试方法加工（熔体）温度285 - 305 °C545- 581 °FDAM
295 °C563 °FDAM; Optimum模具温度70.0 - 120 °C158 - 248 °FDAM
100 °C212 °FDAM; optimum干燥温度80.0 °C176 °FDAM干燥时间2.00 - 4.00hour2.00 - 4.00 hourDAM水分含量<= 0.20 %<= 0.20 %DAM