CYCOLOY™ MC8002 resin 物性表
基本信息特性
低粘度
抗撞击性，高
延展性
用途汽车领域的应用
加工方法注射成型
多点数据Coefficient of Thermal Expansion vs. Temperature (ASTM E831)
Compressive Stress vs. Strain (ASTM D695)
Elastic Modulus vs Temperature (ASTM D4065)
Flexural DMA (ASTM D4065)
Pressure-Volume-Temperature (PVT - Zoller Method)
Shear DMA (ASTM D4065)
Specific Heat vs. Temperature (ASTM D3417)
Tensile Creep (ASTM D2990)
Tensile Fatigue
Tensile Stress vs. Strain (ASTM D638)
Thermal Conductivity vs. Temperature (ASTM E1530)
Viscosity vs. Shear Rate (ASTM D3835)
物理性能额定值单位制测试方法比重1.14g/cm³ASTM D792熔流率（熔体流动速率） (260°C/5.0 kg)9.0g/10 minASTM D1238收缩率 -流动 (3.20 mm)0.50 到0.70%内部方法吸水率ASTM D570 24hr0.10%ASTM D570 平衡, 23°C0.40%ASTMD570机械性能额定值单位制测试方法拉伸模量 12210MPaASTMD638抗张强度 2(屈服)56.5MPaASTM D638伸长率 3
ASTM D638 屈服5.0%ASTMD638 断裂150%ASTMD638弯曲模量 4(50.0 mm跨距)2340MPaASTM D790弯曲强度 5(屈服, 50.0 mm 跨距)86.2MPaASTMD790冲击性能额定值单位制测试方法悬壁梁缺口冲击强度
ASTM D256 -30°C530J/mASTMD256 23°C640J/mASTM D256装有测量仪表的落镖冲击
ASTM D3763 -30°C,Total Energy54.2JASTMD3763 23°C, TotalEnergy61.0JASTM D3763热性能额定值单位制测试方法载荷下热变形温度
ASTM D648 0.45 MPa,未退火, 3.20 mm124°CASTMD648 1.8 MPa, 未退火,3.20 mm107°CASTM D648 1.8 MPa, 未退火, 6.40 mm110°CASTM D648线形热膨胀系数 -流动 (-40 到 40°C)7.2E-5cm/cm/°CASTME831导热系数0.20W/m/KASTM C177注射额定值单位制
干燥温度104 到 110°C
干燥时间3.0 到 4.0hr
干燥时间，Zui大8.0hr
建议的Zui大水分含量0.040%
建议注射量30 到 80%
料筒后部温度249 到 288°C
料筒中部温度254 到 293°C
料筒前部温度260 到 302°C
射嘴温度274 到 302°C
加工（熔体）温度274 到 302°C
模具温度60 到 88°C
背压0.345 到 0.689MPa
螺杆转速40 到 70rpm
排气孔深度0.038 到 0.076mm