原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 23℃,50%RH,24Hr | ASTM D-570 | 0.10 | % |
| 物理性能 | 比重 | 23℃ | ASTM D-792 | 1.08 | --- |
| 成型收缩率 | --- | ASTM D-955 | 0.5-0.7 | % | |
| 机械性能 | 抗拉强度 | 23℃,50%RH | ASTM D-638 | 700 | Kg/cm2 |
| 断裂伸展率 | 23℃,50%RH | ASTM D-638 | 50 | % | |
| 弯曲强度 | 23℃,50%RH | ASTM D-790 | 1000 | Kg/cm2 | |
| 弯曲模量 | 23℃,50%RH | ASTM D-790 | 25000 | Kg/cm2 | |
| 悬臂梁式冲击强度 | 6.4mm带切口23℃ | ASTM D-256 | 15 | kg cm/cm | |
| 电气性能 | 介电系数 | 23℃,50%RH,108Hz | ASTM D-150 | 2.7 | --- |
| 介电正切 | 23℃,50%RH,108Hz | ASTM D-150 | 0.0027 | --- | |
| 表面电阻率 | 23℃,50%RH | ASTM D-257 | 1018 | Ω | |
| 体积电阻率 | 23℃,50%RH | ASTM D-257 | 1018 | Ω.cm | |
| 介电击穿强度 | 短时间法2mm厚 | ASTM D-149 | 26 | KV/mm | |
| 耐电弧性 | 钨电极 | ASTM D-495 | 70 | Secretary | |
| 热 性 能 | 抗燃性 | 1.6mm | UL-94 | V-0 | --- |
| 热变形温度 | 18.6Kg/cm2 | ASTM D-648 | 120 | ℃ | |
Xyron日本旭化成PPE 540Z