PET美国杜邦 FR543玻纤增强43阻燃V-0
物理性能额定值 (公制)额定值 (英制)测试方法比重1.79 g/cc1.79 g/ccASTM D792密度1.79g/cc0.0647 lb/in³ISO 1183填料含量43 %43 %Water Absorption0.060 %
@Temperature 23.0 °C
0.060 %@Temperature 73.4 °F
50%RH,23°C,24h; ASTM D5700.11 %
@Temperature 23.0 °C
0.11 %@Temperature 73.4 °F
E 50%RH; ISO 62, Similar to0.62 %
@Temperature 23.0 °C
0.62 %@Temperature 73.4 °F
Saturation, immersed; ISO 62, Similar to线性成型收缩率0.0013 cm/cm@Thickness 1.57 mm
0.0013 in/in@Thickness 0.0618 in
Flow0.0020 cm/cm
@Thickness 3.20 mm
0.0020 in/in@Thickness 0.126 in
Flow0.0048 cm/cm
@Thickness 1.57 mm
0.0048 in/in@Thickness 0.0618 in
Transverse0.0065 cm/cm
@Thickness 3.20 mm
0.0065 in/in@Thickness 0.126 in
Transverse线性成型收缩率,Flow0.0025 cm/cm0.0025 in/inAnnealed; ISO294-40.0020 cm/cm
@Thickness 2.00 mm
0.0020 in/in@Thickness 0.0787 in
ISO 294-4线性成型收缩率,横向0.0105 cm/cm0.0105 in/inAnnealed; ISO 294-40.0075 cm/cm
@Thickness 2.00 mm
0.0075 in/in@Thickness 0.0787 in
ISO 294-4化合物熔体指数6.0 g/10 min@Load 2.16 kg, Temperature 280 °C
6.0 g/10 min@Load 4.76 lb, Temperature 536 °F
cm3/10 min; ISO 1133机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度(M 级)9595ASTMD785102102ISO 2039/2洛氏硬度(R 级)120120ASTM D785
122122ISO 2039/2抗张强度(断裂)170 MPa
@Temperature 23.0 °C
24700 psi@Temperature 73.4 °F
ISO 527抗张强度55.2 MPa@Temperature 150 °C
8010 psi@Temperature 302 °F
ASTM D63886.5 MPa
@Temperature 90.0 °C
12500 psi@Temperature 194 °F
ASTM D638172 MPa
@Temperature 23.0 °C
24900 psi@Temperature 73.4 °F
ASTM D638210 MPa
@Temperature -40.0 °C
30500 psi@Temperature -40.0 °F
ASTM D63822.4 MPa
@Strain 0.470 %, Temperature 150 °C
3250 psi@Strain 0.470 %, Temperature 302 °F
ISO 52727.22 MPa
@Strain 0.430 %, Temperature 120 °C
3948 psi@Strain 0.430 %, Temperature 248 °F
ISO 52727.5 MPa
@Strain 0.160 %, Temperature 0.000 °C
3990 psi@Strain 0.160 %, Temperature 32.0 °F
ISO 52728.39 MPa
@Strain 0.350 %, Temperature 90.0 °C
4118 psi@Strain 0.350 %, Temperature 194 °F
ISO 52729.0 MPa
@Strain 0.140 %, Temperature -40.0 °C
4210 psi@Strain 0.140 %, Temperature -40.0 °F
ISO 52730.0 MPa
@Strain 0.210 %, Temperature 40.0 °C
4350 psi@Strain 0.210 %, Temperature 104 °F
ISO 52731.0 MPa
@Strain 0.180 %, Temperature 23.0 °C
4500 psi@Strain 0.180 %, Temperature 73.4 °F
ISO 52734.9 MPa
@Strain 0.940 %, Temperature 150 °C
5060 psi@Strain 0.940 %, Temperature 302 °F
ISO 52735.57 MPa
@Strain 0.310 %, Temperature 60.0 °C
5159 psi@Strain 0.310 %, Temperature 140 °F
ISO 52741.5 MPa
@Strain 1.41 %, Temperature 150 °C
6020 psi@Strain 1.41 %, Temperature 302 °F
ISO 52741.8 MPa
@Strain 0.830 %, Temperature 120 °C
6060 psi@Strain 0.830 %, Temperature 248 °F
ISO 52745.7 MPa
@Strain 1.87 %, Temperature 150 °C
6630 psi@Strain 1.87 %, Temperature 302 °F
ISO 52747.19 MPa
@Strain 0.690 %, Temperature 90.0 °C
6844 psi@Strain 0.690 %, Temperature 194 °F
ISO 52749.1 MPa
@Strain 2.34 %, Temperature 150 °C
7120 psi@Strain 2.34 %, Temperature 302 °F
ISO 52750.35 MPa
@Strain 0.370 %, Temperature 40.0 °C
7303 psi@Strain 0.370 %, Temperature 104 °F
ISO 52750.8 MPa
@Strain 1.23 %, Temperature 120 °C
7370 psi@Strain 1.23 %, Temperature 248 °F
ISO 52751.7 MPa
@Strain 2.81 %, Temperature 150 °C
7500 psi@Strain 2.81 %, Temperature 302 °F
ISO 52752.4 MPa
@Strain 0.320 %, Temperature 0.000 °C
7600 psi@Strain 0.320 %, Temperature 32.0 °F
ISO 52753.8 MPa
@Strain 3.28 %, Temperature 150 °C
7800 psi@Strain 3.28 %, Temperature 302 °F
ISO 52753.9 MPa
@Strain 0.280 %, Temperature -40.0 °C
7820 psi@Strain 0.280 %, Temperature -40.0 °F
ISO 52755.0 MPa
@Strain 0.520 %, Temperature 60.0 °C
7980 psi@Strain 0.520 %, Temperature 140 °F
ISO 52755.6 MPa
@Strain 3.75 %, Temperature 150 °C
8060 psi@Strain 3.75 %, Temperature 302 °F
ISO 52756.4 MPa
@Strain 0.350 %, Temperature 23.0 °C
8180 psi@Strain 0.350 %, Temperature 73.4 °F
ISO 52756.85 MPa
@Strain 1.63 %, Temperature 120 °C
8245 psi@Strain 1.63 %, Temperature 248 °F
ISO 52757.1 MPa
@Strain 4.21 %, Temperature 150 °C
8280 psi@Strain 4.21 %, Temperature 302 °F
ISO 52758.5 MPa
@Strain 4.69 %, Temperature 150 °C
8480 psi@Strain 4.69 %, Temperature 302 °F
ISO 52759.61 MPa
@Strain 1.03 %, Temperature 90.0 °C
8646 psi@Strain 1.03 %, Temperature 194 °F
ISO 52761.26 MPa
@Strain 2.04 %, Temperature 120 °C
8885 psi@Strain 2.04 %, Temperature 248 °F
ISO 52764.62 MPa
@Strain 2.44 %, Temperature 120 °C
9372 psi@Strain 2.44 %, Temperature 248 °F
ISO 52767.28 MPa
@Strain 2.84 %, Temperature 120 °C
9758 psi@Strain 2.84 %, Temperature 248 °F
ISO 52768.2 MPa
@Strain 1.37 %, Temperature 90.0 °C
9890 psi@Strain 1.37 %, Temperature 194 °F
ISO 52769.36 MPa
@Strain 3.24 %, Temperature 120 °C
10060 psi@Strain 3.24 %, Temperature 248 °F
ISO 52771.09 MPa
@Strain 3.65 %, Temperature 120 °C
10310 psi@Strain 3.65 %, Temperature 248 °F
ISO 52771.87 MPa
@Strain 0.730 %, Temperature 60.0 °C
10420 psi@Strain 0.730 %, Temperature 140 °F
ISO 52772.35 MPa
@Strain 4.05 %, Temperature 120 °C
10490 psi@Strain 4.05 %, Temperature 248 °F
ISO 52772.8 MPa
@Strain 0.560 %, Temperature 40.0 °C
10600 psi@Strain 0.560 %, Temperature 104 °F
ISO 52774.5 MPa
@Strain 0.480 %, Temperature 23.0 °C
10800 psi@Strain 0.480 %, Temperature 73.4 °F
ISO 52774.52 MPa
@Strain 1.70 %, Temperature 90.0 °C
10810 psi@Strain 1.70 %, Temperature 194 °F
ISO 52775.5 MPa
@Strain 0.420 %, Temperature -40.0 °C
11000 psi@Strain 0.420 %, Temperature -40.0 °F
ISO 52775.9 MPa
@Strain 0.470 %, Temperature 0.000 °C
11000 psi@Strain 0.470 %, Temperature 32.0 °F
ISO 52779.34 MPa
@Strain 2.04 %, Temperature 90.0 °C
11510 psi@Strain 2.04 %, Temperature 194 °F
ISO 52783.14 MPa
@Strain 2.41 %, Temperature 90.0 °C
12060 psi@Strain 2.41 %, Temperature 194 °F
ISO 52783.19 MPa
@Strain 0.940 %, Temperature 60.0 °C
12070 psi@Strain 0.940 %, Temperature 140 °F
ISO 52785.76 MPa
@Strain 2.75 %, Temperature 90.0 °C
12440 psi@Strain 2.75 %, Temperature 194 °F
ISO 527