美国杜邦的POM 900P属于纤维级，一般用于包装容器-塑料容器-薄壁制品，Low Viscosity AcetalHomopolymer with Improved Processing
POM是合成树脂中的一种，又名聚甲醛树脂、POM塑料、赛钢料等；是一种白色或黑色塑料颗粒，具有高硬度、高钢性、高耐磨的特性。主要用于齿轮，轴承，汽车零部件、机床、仪表内件等起骨架作用的产品。
杜邦公司采用机械共混和接枝共聚的方法开发出超韧性POM/PUR-T合金，既保持了POM的强度和刚性，又提高了POM的耐冲击性，其缺口冲击强度比纯POM提高17倍，达到906J/m。四川大学白时兵等5发现采用以CaCO3为核、PUR-T为壳的PUR-T/CaCO3超细复合粉体增韧POM，其缺口冲击强度大大提高。于建等对其研究表明，PUR-T包覆CaCO3粒子的粒间距达到临界值Tc≤0.18μm，包覆层厚度达到临界值Lc≥0.7μm时，共混POM材料发生脆-韧转变，材料的冲击强度可比纯POM提高数十倍，拉伸强度可达30MPa左右。
POM has regular molecular structure, high crystallinity and highsurface hardness. In the process of friction and sliding, itsmacromolecule is easy to be oriented and strengthened along thedirection of friction, with large bond energy and high molecularcohesion energy, so POM has good wear resistance andself-lubrication performance. However, it is difficult to meet therequirements of high load, high speed, high temperature and otherworking conditions, so the wear resistance of POM needs to befurther improved. There are two ways to improve the wear resistanceof POM: one is chemical modification. Lubricating segments wereintroduced into POM molecular chains by means of grafting andblock. The other is physical blending modification. Duracon NW-02,developed by Japan Plastics Company, is a lubricating modifier madeof a lubricating polymer grafted with POM. Under the same load andsliding speed, the sliding surface temperature of Duracon NW-02 is30%-50% lower than that of the unmodified POM
POM的注塑成型工艺：
一、POM吸水性小，一般为0.2%-0.5%。在通常情况下，POM不需干燥就能加工，但对潮湿原料必须进行干燥。干燥温度80℃，时间2小时以上，具体应按供应商资料进行。 再生料使用比例一般不超过20-30%。但要视产品的种类和Zui终用途而定，有时可达。
二、塑机的选用 POM除了要求螺杆无滞料区外，对注塑机没有特别要求，一般注塑即可。
三、熔胶温度 可用空射法量度 POM-H 可设为215℃ （190℃-230℃） POM-K 可设为205℃ （190℃-210℃）
四、背压 越低越好，一般不超过200bar POM-H 可在215℃滞留35分钟 POM-K 可在205℃滞留20分钟不会有严重的分解 在注塑温度下熔体不能在机筒内滞留超过20分钟。POM-K在240℃下可滞留7分钟。如果停机，机筒温度可降到150℃，如要长期停机就必须清理机筒子，关闭加热器。
五、停机 清理机筒必须用PE或PP，关闭电热，把螺杆推在前位。料筒和螺杆必须保持清洁。杂质或污垢会改变POM的过热稳定性（尤其是POM-H）。当用完含卤聚合物或其他酸性聚合物后，应用PE清理干净后才能打POM料，否则会发生爆炸。若作用不当的颜料、润滑剂或含GF尼龙的物料，会导致塑料降质。