ASTM D638/ISO 52761.8kg/cm²(MPa)[Lb/in2]断裂伸长率
ASTM D638/ISO 527>%拉伸模量
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in2]拉伸屈服伸长率(延伸率)
ASTM D638/ISO 527
%拉伸断裂伸长率(延伸率)
ASTM D638/ISO 527>%弯曲模量(弯曲弹性率)
ASTM D790/ISO 1782260kg/cm²(MPa)[Lb/in2]弯曲强度
ASTM D790/ISO 17895.1kg/cm²(MPa)[Lb/in2]洛氏硬度
ASTM D785118
IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 179760kg·cm/cm(J/M)ft·lb/in1/4"-30℃ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ (缺口)ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in-30℃(缺口)ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in23℃(无缺口)ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in-30℃(无缺口)ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in物性性能比重(密度)
ASTM D792/ISO 11831.21
成型收缩率
ASTM D9550.5-0.7%%熔融指数(流动系数)200℃/5kgASTM D1238/ISO113312g/10min220℃/10kgASTM D1238/ISO 1133
g/10min吸水率 23℃/24H
ASTM D570/ISO 62
%热性能热变形温度退火ASTM D648/ISO 75
℃(℉)未退火ASTM D648/ISO 75130℃(℉)维卡软化点
ASTM D1525/ISO R306140℃(℉)熔点
-
℃(℉)燃烧性(率)
UL94V-0
线性膨胀系数
ASTM D696/ISO 11359
mm/mm.℃电气性能介电常数100HZASTM D150/IEC 60250
1MHZASTM D150/IEC 60250
介电损耗100HZASTM D150/IEC 60250
1MHZASTM D150/IEC 60250
体积电阻率
ASTM D257/IEC 60093
Ω.cm表面电阻率
ASTM D257/IEC 60093
Ω耐电弧性
ASTM D495/IEC 60112
光学性能折射率
ASTM D542/ISO 489
透光率
ASTM D1003/ISO 13468
%模糊系数(Haze)
ISO 14782
%加工条件干燥条件
100-120度 3-5H
加工温度射嘴
300-320℃料筒前段
300-320℃料筒中段
280-300℃料筒后段
260-280℃熔体温度
300-320℃模具温度
80-100℃压力注塑压力
Mpa保压压力
Mpa背压
0.981-3.92Mpa螺杆转速
40-70rpm