LNP Thermocomp® HF-1006 Polyamide 11, Glass Fiber Reinforcement物性表
物理性能额定值 (公制)额定值 (英制)测试方法| 比重 | 1.26 g/cc | 1.26 g/cc | Method A; ASTM D792 |
| 吸水率 | 0.10 % | 0.10 % | at 24 hrs; ASTM D570 |
| 线性成型收缩率 | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| 线性成型收缩率，横向 | 0.0060 - 0.0070 cm/cm | 0.0060 - 0.0070 in/in | ASTM D955 |
| 抗张强度(断裂) | 134 MPa | 19400 psi | ASTM D638 |
| 抗张强度(屈服) | 134 MPa | 19400 psi | ASTM D638 |
| 伸长率 (断裂) | 6.2 % | 6.2 % | ASTM D638 |
| 屈服伸长率 | 5.3 % | 5.3 % | ASTM D638 |
| 拉伸模量 | 7.38 GPa | 1070 ksi | ASTM D638 |
| 弯曲强度 | 193 MPa | 28000 psi | ASTM D790 |
| 弯曲模量 | 6.21 GPa | 901 ksi | ASTM D790 |
| 悬壁梁缺口冲击强度 | 2.56 J/cm @Thickness 3.18 mm | 4.80 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| 悬壁梁无缺口冲击强度 | 14.3 J/cm @Thickness 3.18 mm | 26.8 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| 悬壁梁缺口冲击强度 | 25.3 kJ/m² | 12.0 ft-lb/in² | ISO 180 |
| 悬壁梁无缺口冲击强度 | 87.8 kJ/m² | 41.8 ft-lb/in² | ISO 180 |
| Falling Dart Impact | 16.7 J | 12.3 ft-lb | ASTM D3763 |
| 冲击试验 | 6.72 J | 4.96 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |