供应韩国LG XR404超高耐热ABS显示出优良的耐热性以及冲击强度、刚性、可加工性

Density / Specific Gravity 2

1.05

g/cm³

Density (23°C)

1.05

g/cm³

Melt Mass-Flow Rate (MFR) (220°C/10.0 kg)

7.0

g/10 min

Melt Mass-Flow Rate (MFR) (220°C/10.0 kg)

7.0

g/10 min

Molding Shrinkage - Flow (23°C, 3.20 mm, Injection Molded)

0.40 to 0.70

%

Molding Shrinkage (23°C, 3.20 mm)

0.40 to 0.70

%

Tensile Modulus 3 (23°C, 3.20 mm, Injection Molded)

2500

MPa

Tensile Strength 3 (Yield, 23°C, 3.20 mm, Injection Molded)

52.0

MPa

Tensile Stress (Yield, 23°C, 4.00 mm, Injection Molded)

54.0

MPa

Tensile Elongation 3 (Break, 23°C, 3.20 mm, Injection Molded)

> 15

%

Tensile Strain (Break, 23°C, 4.00 mm, Injection Molded)

> 15

%

Flexural Modulus 4 (23°C, 3.20 mm, Injection Molded)

2650

MPa

Flexural Modulus 5 (23°C, 4.00 mm, Injection Molded)

2550

MPa

Flexural Strength 4 (23°C, 3.20 mm, Injection Molded)

84.0

MPa

Flexural Stress 5 (23°C, 4.00 mm, Injection Molded)

82.0

MPa

Charpy Notched Impact Strength 6

Notched Izod Impact

Notched Izod Impact Strength 6

Rockwell Hardness (R-Scale, 23°C, Injection Molded)

112

Rockwell Hardness (R-Scale, 23°C)

114

Deflection Temperature Under Load 7 (0.45 MPa, Unannealed, 6.40 mm, Injection Molded)

108

°C

Deflection Temperature Under Load (0.45 MPa, Unannealed, 4.00 mm)

101

°C

Deflection Temperature Under Load 7 (0.45 MPa, Annealed, 6.40 mm)

111

°C

Deflection Temperature Under Load (0.45 MPa, Annealed, 4.00 mm)

106

°C

Deflection Temperature Under Load 7 (1.8 MPa, Unannealed, 6.40 mm, Injection Molded)

100

°C

Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm)

93.0

°C

Deflection Temperature Under Load 7 (1.8 MPa, Annealed, 6.40 mm, Injection Molded)

106

°C

Deflection Temperature Under Load (1.8 MPa, Annealed, 4.00 mm)

101

°C

Vicat Softening Temperature

112

°C

Vicat Softening Temperature

112

°C

Flame Rating