| ExxonMobil™ EVA 400028.EM1 | Units SI English |
| Ethylene Vinyl AcetateCopolymer |
| Product DescriptionExxonMobil™ EVA 400028.EM1 is acopolymer of ethylene and vinyl acetate. |
| General | |
Availability 1 | Africa & Middle EastAsia PacificEurope |
Additive | Antiblock: NoSlip: NoThermal Stabilizer: YesFree Flowing Agent:Yes |
Applications | Hot Melt AdhesivesWire and Cable Compounds |
Form(s) |
|
Revision Date |
|
| Resin Properties | Typical Value | Unit | Test Based On |
Density | 0.948 | g/cm³ | ASTM D1505 |
Melt Index 2 (190°C/2.16 kg) | 400 | g/10 min | ASTM D1238 |
Vinyl Acetate Content | 28.0 | wt% | ExxonMobil Method |
Peak Melting Temperature | 67 | °C | ExxonMobil Method |
| Molded Properties | Typical Value | Unit | Test Based On |
Tensile Modulus (5.0 mm/min) | 11 | MPa | ASTM D638 |
Tensile Strength atBreak (500 mm/min) | 2.4 | MPa | ASTM D638 |
Elongation at Break (500 mm/min) | 580 | % | ASTM D638 |
Durometer Hardness (Shore A) | 73 | ASTM D2240 |