低挥发 POM 塞拉尼斯 C9021 XAP 高硬度 耐燃油汽车零部件应用
Hostaform®C 9021 XAP®
Acetal (POM) Copolymer
Celanese Corporation
产品说明：
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 03-002
POM copolymer
Product with reduced emissions especially for automotive interiorapplication. Good properties of the standard-injection moldinggrades like high rigidity, hardness and toughness; good chemicalresistance to solvents, fuel and strong alkalis as well as goodhydrolysis resistance; high resistance to thermal and oxidativedegradation are maintained
Monomers and additives are listed in EU-Regulation (EU) 10/2011
FDA compliant according to 21 CFR 177.2470
Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thicknessmore than 1 mm.
Ranges of applications: automotive engineering,
FDA = Food and Drug Administration (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 加工方法 |
|
| 树脂ID (ISO 1043) |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.41 | g/cm³ | ISO 1183 |
| 溶化体积流率（MVR） (190°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| 收缩率 | ISO 294-4 | ||
| 垂直流动方向 | 1.8 | % | ISO 294-4 |
| 流动方向 | 2.0 | % | ISO 294-4 |
| 吸水率 (饱和, 23°C) | 0.65 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 2850 | MPa | ISO 527-2/1A/1 |
| 拉伸应力 (屈服) | 64.0 | MPa | ISO 527-2/1A/50 |
| 拉伸应变 (屈服) | 9.0 | % | ISO 527-2/1A/50 |
| 标称拉伸断裂应变 | 30 | % | ISO 527-2/1A/50 |
| 拉伸蠕变模量 | ISO 899-1 | ||
| 1 hr | 2500 | MPa | ISO 899-1 |
| 1000 hr | 1300 | MPa | ISO 899-1 |
| 弯曲模量 (23°C) | 2700 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.5 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度 | ISO 179/1eU | ||
| -30°C | 160 | kJ/m² | ISO 179/1eU |
| 23°C,局部断裂 | 180 | kJ/m² | ISO 179/1eU |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度 (1.8 MPa, 未退火) | 104 | °C | ISO 75-2/A |
| 熔融温度 1 | 166 | °C | ISO 11357-3 |
| 线形热膨胀系数 | ISO 11359-2 | ||
| 流动 | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| 横向 | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 表面电阻率 | 1.0E+14 | ohms | IEC 60093 |
| 体积电阻率 | 1.0E+14 | ohms·cm | IEC 60093 |
| 介电强度 | 35 | kV/mm | IEC 60243-1 |
| 相对电容率 | IEC 60250 | ||
| 100 Hz | 4.00 | IEC 60250 | |
| 1 MHz | 4.00 | IEC 60250 | |
| 耗散因数 | IEC 60250 | ||
| 100 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 5.0E-3 | IEC 60250 | |
| 漏电起痕指数 | 600 | V | IEC 60112 |
低挥发 POM 塞拉尼斯 C9021 XAP 高硬度 耐燃油 汽车零部件应用