聚亚己基己二酸酰胺#聚己二酰己二胺|尼龙66|PA66
日本宇部
物性信息：
| 基本性能 | 额定值 | 单位 | 测试方法 |
|---|
| 吸水率 |
|
| ASTM D-570 |
| 1.0 | % |
|
| 6.6 | % |
|
| 成型收缩率 |
|
| UBEmethod |
| 0.6 | % |
|
| 1.4 | % |
|
| 机械性能 | 额定值 | 单位 | 测试方法 |
|---|
| 弯曲弹性率 (23°) | 65000 | kgf/cm | ASTM D-790 |
| 硬度(洛氏.布氏) (23°) | 95 |
| ASTM D-785 |
| 屈服下的伸张强度 (23°) | 950 | kgf/cm | ASTM D-638 |
| 弯曲弹性率 (23°) | 40000 | kgf/cm | ASTM D-790 |
| 屈服下的伸张强度 (23°) | 1550 | kgf/cm | ASTM D-638 |
| 硬度(洛氏.布氏) |
|
| ASTM D-785 |
| (23°) | 120 |
|
|
| (23°) | 113 |
|
|
| 抗冲击强度 (23°) | 10 | kgf.cm/cm | ASTM D-256 |
| 弯曲强度 |
|
| ASTM D-790 |
| (23°) | 1400 | kgf/cm |
|
| (23°) | 2200 | kgf/cm |
|
| 抗冲击强度 (23°) | 7.0 | kgf.cm/cm | ASTM D-256 |
| 断裂下的延伸率 (23°) | 5 | % | ASTM D-638 |
| 电气性能 | 额定值 | 单位 | 测试方法 |
|---|
| 绝缘耐力 | 2 | KV/mm | ASTM D-149 |
| 体积电阻率 | 10 | Ω.cm | ASTM D-257 |
| 介电损耗 (10HZ) | 0.01 |
| ASTM D-150 |
| 介电常数 |
|
| ASTM D-150 |
| (10HZ) | 4.0 |
|
|
| (10HZ) | 3.6 |
|
|
| IEC电路 | 600+ | V | UL 746 |
| 介电常数 (60HZ) | 4.1 |
| ASTM D-150 |
| 介电损耗 (60HZ) | 0.01 |
| ASTM D-150 |
| 抗电弧强度 | 151 | S | ASTM D-495 |
| 体积电阻率 | 10 | Ω.cm | ASTM D-257 |
| 介电损耗 (10HZ) | 0.02 |
| ASTM D-150 |
| 热性能 | 额定值 | 单位 | 测试方法 |
|---|
| 熔点 (DSC) | 215-225 | °C |
|
| 热变形温度 (8.6kgf/cm2 ) | 252 | °C | ASTM D-648 |
| 线性热膨胀系数 | 3.5 | X的10-5cm/cm/°C | ASTM D-696 |
| 燃烧率 | HB |
| UL 94 |
聚亚己基己二酸酰胺#聚己二酰己二胺|尼龙66|PA66