Polycarbonate
SABIC Innovative Plastics
产品说明：
LEXAN 945A Polycarbonate (PC) resin is a non-filled, injectionmoldable grade. This non-chlorinated, non-brominated flameretardant PC has an UL-94 V0 rating and is available in transparentand tinted color options. LEXAN 945A is a general purpose resindesigned to meet the needs of various applications.
物性信息：
| 基本信息 |
|
|---|
| | |
| 添加剂 | |
| 特性 | |
| 用途 | |
| 外观 | |
| 加工方法 | |
| 多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 比重 | 1.19 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 (3.20 mm) | 0.60 到 0.80 | % | 内部方法 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 拉伸模量 1 | 2270 | MPa | ASTM D638 |
| 抗张强度 2 |
|
| ASTM D638 |
| 屈服 | 62.0 | MPa | ASTM D638 |
| 断裂 | 67.0 | MPa | ASTM D638 |
| 伸长率 3 |
|
| ASTM D638 |
| 屈服 | 6.0 | % | ASTM D638 |
| 断裂 | 130 | % | ASTM D638 |
| 弯曲模量 4(50.0mm 跨距) | 2370 | MPa | ASTM D790 |
| 弯曲强度 5(屈服,50.0 mm 跨距) | 101 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 悬壁梁缺口冲击强度 (23°C) | 800 | J/m | ASTM D256 |
| 装有测量仪表的落镖冲击 (23°C, TotalEnergy) | 79.0 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 |
|
| ASTM D648 |
| 0.45 MPa, 未退火, 3.20mm | 137 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 3.20mm | 126 | °C | ASTM D648 |
| 维卡软化温度 | 143 | °C | ASTM D1525 6 |
| 线形热膨胀系数 |
|
| ASTM E831 |
| 流动 : -40 到40°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| 横向 : -40 到40°C | 7.4E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 耐电弧性 7 | PLC 7 |
| ASTM D495 |
| 相比耐漏电起痕指数(CTI) | PLC 2 |
| UL 746 |
| 高电弧燃烧指数(HAI) | PLC 3 |
| UL 746 |
| 高电压电弧起痕速率 (HVTR) | PLC 3 |
| UL 746 |
| 热丝引燃 (HWI) | PLC 2 |
| UL 746 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|
| UL 阻燃等级 |
|
| UL 94 |
| 0.800 mm | V-2 |
| UL 94 |
| 3.04 mm | V-0 |
| UL 94 |
| 灼热丝易燃指数 (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| 热灯丝点火温度 (1.00 mm) | 850 | °C | IEC 60695-2-13 |
| 极限氧指数 | 35 | % | ISO 4589-2 |
| 注射 | 额定值 | 单位制 |
|
|---|
| 干燥温度 | 120 | °C |
|
| 干燥时间 | 2.0 到 4.0 | hr |
|
| 建议的Zui大水分含量 | 0.020 | % |
|
| 料斗温度 | 60.0 到 80.0 | °C |
|
| 料筒后部温度 | 260 到 280 | °C |
|
| 料筒中部温度 | 270 到 290 | °C |
|
| 料筒前部温度 | 280 到 310 | °C |
|
| 射嘴温度 | 270 到 290 | °C |
|
| 加工（熔体）温度 | 280 到 310 | °C |
|
| 模具温度 | 80.0 到 110 | °C |
|