| C/ABS C2950 -111 基础创新塑料(南沙)物性数据 |
| 规格级别： | --- | 外观颜色： | --- |
| 用途概述： | --- | ||
| 备注说明： | 特性：阻燃V0，耐高温 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.18 | --- |
| 吸水率 | --- | ASTM D-570 | 0.1 | % | |
| 模具收缩率 | 3.2mm | ASTM D-955 | 4-6 | E-3 | |
| 机械性能 | 拉伸强度(屈伏点) | --- | ASTM D-638 | 63 | Mpa |
| 拉伸率(断裂点) | --- | ASTM D-638 | 40 | % | |
| 拉伸模量 | --- | ASTM D-638 | - | Mpa | |
| 弯曲强度 | --- | ASTM D-790 | 102 | Mpa | |
| 弯曲模量 | --- | ASTM D-790 | 2653 | Mpa | |
| 冲击强度缺口 | 23℃ | ASTM D-256 | 533 | J/m | |
| 洛氏硬度 | --- | D785 | 123 | R | |
| 电气性能 | 损耗因数 | 1MHz | ASTM D-150 | - | --- |
| 介电常数 | 1MHz | ASTM D-150 | - | --- | |
| 体积电阻 | --- | ASTM D-150 | 1.0E+17 | Ohm-cm | |
| 表面电阻 | --- | ASTM D-257 | 1.0E+16 | Ohm-cm | |
| 热 性 能 | 阻燃性 | --- | UL-94 | V-0 | --- |
| 阻燃性 | --- | UL-94 | 1.6 | mm | |
| 热变形温度 | 0.45Mpa | ASTM D-648 | 104 | ℃ | |
| 热变形温度 | 1.8Mpa | ASTM D-648 | 95 | ℃ | |
| 维卡软化点 | --- | ASTM D-1525 | 112 | ℃ | |
| 线膨胀系数 | --- | E-831 | - | 1/℃ | |
| UL长期使用温度 | 含冲击 | UL-746B | 75 | ℃ | |
| UL长期使用温度 | 无冲击 | UL-746B | 85 | ℃ | |
PC/ABS，聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物和混合物，是由聚碳酸酯（Polycarbonate）和聚丙烯精（ABS）合金而成的热可塑性塑胶，结合了两种材料的优异特性，ABS材料的成型性和PC的机械性、冲击强度和耐温、抗紫外线（UV）等性质，可广泛使用在汽车内部零件、事务机器、通信器材、家电用品及照明设备上。[1][2]
典型应用范围:手机外壳、计算机和商业机器壳体、电器设备、草坪园艺机器、汽车零件仪表板、内部装修以及车轮盖。
注塑模工艺条件:
干燥处理：加工前的干燥处理是必须的。湿度应小于0.04%，建议干燥条件为90~110C，2~4小时。
熔化温度：230~300C。
模具温度：50~100C。
注射压力：取决于塑件。
注射速度：尽可能地高。
化学和物理特性:PC/ABS具有PC和ABS两者的综合特性。例如ABS的易加工特性和PC的优良机械特性和热稳定性。二者的比率将影响PC/ABS材料的热稳定性。PC/ABS这种混合材料还显示了优异的流动特性。收缩率在0.5%左右。
特点
PC/ABS是一种通过混炼后合成的改性工程塑料。其中，PC就是聚碳酸脂，ABS就是丙烯腈（A）、丁二烯（B）和苯乙烯（S）的共聚物。这种改性塑料比单纯的PC和ABS性能更好，例如：抗冲击性提高，耐热性提高，硬度提高等等。ABS塑料
特点：
1、综合性能较好,冲击强度较高,化学稳定性,电性能良好.
2、与372有机玻璃的熔接性良好,制成双色塑件,且可表面镀铬,喷漆处理.
3、有高抗冲、高耐热、阻燃、增强、透明等级别。
4、流动性比HIPS差一点，比PMMA、PC等好，柔韧性好。