| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTMD792 | 1.18 | g/cm³ | |
| 熔流率（熔体流动速率）(220°C/10.0kg) | ASTMD1238 | 60 | g/10min | ||
| 收缩率-流动(3.20mm) | ASTMD955 | 0.40to0.70 | % | ||
| 机械性能 | 拉伸模量2(3.20mm) | ASTMD638 | 2160 | MPa | |
| 抗张强度3(屈服,3.20mm) | ASTMD638 | 43.1 | MPa | ||
| 伸长率3(屈服,3.20mm) | ASTMD638 | 5.0 | % | ||
| 伸长率3(断裂,3.20mm) | ASTMD638 | >20 | % | ||
| 弯曲模量4(6.40mm) | ASTMD790 | 2550 | MPa | ||
| 弯曲强度4(6.40mm) | ASTMD790 | 68.6 | MPa | ||
| 冲击性能 | 悬壁梁缺口冲击强度 | -30°C,3.20mm | ASTMD256 | 78 | J/m |
| -30°C,6.40mm | ASTMD256 | 78 | J/m | ||
| 23°C,3.20mm | ASTMD256 | 260 | J/m | ||
| 23°C,6.40mm | ASTMD256 | 230 | J/m | ||
| 硬度 | 洛氏硬度(R级) | ASTMD785 | 104 | ||
| 热性能 | 载荷下热变形温度(0.45MPa,未退火,6.40mm) | ASTMD648 | 84.0 | °C | |
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | ASTMD648 | 77.0 | °C | ||
| 维卡软化温度 | ASTMD15255 | 84.0 | °C | ||
| RTIElec | UL746 | 80.0 | °C | ||
| RTIImp | UL746 | 70.0 | °C | ||
| RTIStr | UL746 | 80.0 | °C | ||
| 可燃性 | UL阻燃等级 | 2.5mm | UL94 | V-0 | |
| 3.0mm | UL94 | V-0 | |||
| 产品物性 |
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔指 | 220℃/10kg | ASTM D-1238 | 50 | g/10min |
| 物理性能 | 比重 | ASTM D-792 | 1.18 | ||
| 模具收缩率 | ASTM D-955 | 0.4-0.7 | % | ||
| 机械性能 | 缺口冲击强度 | 23℃，1/8" | ASTM D-256 | 25 | kg.cm/cm |
| 拉伸屈服强度 | 23℃，50mm/min | ASTM D-638 | 430 | Kg/cm2 | |
| 断裂伸长率 | 23℃，50mm/min | ASTM D-638 | 20 | % | |
| 弯曲强度 | 23℃，15mm/min | ASTM D-790 | 710 | Kg/cm2 | |
| 弯曲模量 | 23℃，15mm/min | ASTM D-790 | 26000 | Kg/cm2 | |
| 洛氏硬度 | ASTM D-785 | 102 | R-Scale | ||
| 热性能 | 热变形温度 | 未退火，18.5kg/cm2,1/4" | ASTM D-648 | 76 | ℃ |
| 阻燃等级 | 1/10" | UL 94 | V-0 | ||
| 产品图片 |