UNITHENE®LH606
High Density Polyethylene
USI Corporation
产品说明：
UNITHENE LH606 is a high density polyethylene (HDPE) suitablyused for injection molding and filament applications. Typicalapplications are the injection molding of fruit crates, foodcontainers, industrial items such as pallets, transportationcrates, housewares, toys and the fine filament extrusion ofmosquito nets.
UNITHENE LH606 possesses high impact strength and good resistanceto stress cracking, good stiffness, high hardness, good surfacegloss, less warpage, low shrinkage.
UNITHENE LH606 can be easily pigmented to any color by either dryblending or melt blending of the pigment into the resin. Printingon items molded from UNITHENE LH606 can be easily accomplishedafter a simple flame, chemical or electronic surface treatment.
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.962 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） | 6.0 | g/10 min | ASTM D1238 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 69 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 - 1% 正割 (模压成型) | 971 | MPa | ASTM D638 |
| 抗张强度 | ASTM D638 | ||
| 屈服 | 30.4 | MPa | ASTM D638 |
| 断裂 | 21.6 | MPa | ASTM D638 |
| 伸长率 (断裂) | 600 | % | ASTM D638 |
| 明显的弯曲模量 | 971 | MPa | ASTM D747 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | 69 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 脆化温度 | < -76.0 | °C | ASTM D746 |
| 维卡软化温度 | 127 | °C | ASTM D1525 |
| 熔融峰值温度 | 135 | °C | ASTM D3418 |
高密度聚乙烯塑料原料 - HDPE
百塑烯主要用途为：
注塑成型、铸膜挤压、细圆丝加工、注塑成型（用于制造塑料箱）、淋膜、扁丝加工、粗圆丝加工、薄膜与平板挤压。
LH503 
注塑成型
LH506 注塑成型
LH514 注塑成型
铸膜挤压
LH523 注塑成型
LH606 注塑成型
细圆丝加工
LH606-13 注塑成型（用于制造塑料箱）
LH608 注塑成型
淋膜
LH614 注塑成型
铸膜挤压
LH901 扁丝加工
粗圆丝加工
薄膜与平板挤压
注：Zui新报价及其对该信息的图片和价格有疑问，敬请电联我公司恰谈，欢迎你的来电！！！